Eurostar Starflam M10009XP PP, Flame Retardant, Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam M10009XP PP, Flame Retardant, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam M10009XP is an Unfilled Flame Retardant Polypropylene (Copolymer) Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ISO 1183 |
| Water Absorption | 0.010 % @Temperature 23.0 °C, Time 86400 sec |
0.010 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.016 cm/cm @Thickness 4.00 mm |
0.016 in/in @Thickness 0.157 in |
E2P method |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ISO 527 |
| Elongation at Break | 125 % | 125 % | ISO 527 |
| Tensile Modulus | 1.40 GPa | 203 ksi | 50 mm/min; ISO 527 |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ISO 178 |
| Izod Impact, Unnotched (ISO) | >= 98.0 kJ/m² | >= 46.6 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Glow Wire Test | 850 °C @Thickness 1.60 mm |
1560 °F @Thickness 0.0630 in |
IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 190 °C | 356 - 374 °F | |
| Zone 2 | 190 - 200 °C | 374 - 392 °F | |
| Zone 3 | 190 - 200 °C | 374 - 392 °F | |
| Melt Temperature | 190 - 200 °C | 374 - 392 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- Victrex® PEEK 450CA40 Polyetheretherketone, 40% Carbon Fibre Reinforced
- Overview of materials for Styrene-Butadiene Copolymer, SBC
- Mitsubishi Xantar® G4F 22 UR Polycarbonate-20% Glass Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP KFL34XXC Acetal Copolymer (Europe-Africa-Middle East)
- Solvay Chemicals SOLKANE® 365/227 Blends
- Samyang Triloy® 200NH PC/ABS alloy, Flame Retardant
- Solvay TECHNYL® A 216 NATURAL FA PA66, Conditioned
- Braskem UTEC® 4041 Ultra High Molecular Weight Polyethylene
- 3M Scotchlite™ IJ5100R-10 Reflective Graphic Film
- Resinlab® EP1285HD-14 Highly Filled, Medium Viscosity Casting Resin
Copyright © lookpolymers.com All Rights Reserved