Gromax 1155LL TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax 1155LL TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
1155LL is medium modulus grade with nominal Durometer hardness of 55D. It contains color stable antioxidants. It can be processed by thermoplastic processing techniques like injection molding and extrusion molding grade.Characteristics:Excellent low modulus for injection molding and extrusion molding grade.Excellent flexibility and fatigue resistance.Excellent creep resistance.Excellent low shrinkage and higher melting temperatureInformation provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.193 g/cc | 1.193 g/cc | ISO 1183 |
| Moisture Absorption | 0.400 % @Time 86400 sec |
0.400 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.065 cm/cm | 0.065 in/in | ISO 294-4 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
30 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | ISO 868 |
| Tensile Strength | 23.5 MPa | 3410 psi | ISO 527 |
| Elongation at Break | 466 % | 466 % | ISO 527 |
| Tensile Modulus | 0.421 GPa | 61.1 ksi | ISO 527 |
| Flexural Modulus | 0.122 GPa | 17.6 ksi | ISO 178 |
| Charpy Impact, Notched | NB | NB | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 209 °C | 408 °F | ISO 3146C |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.13e+13 ohm-cm | 2.13e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 3.57e+13 ohm | 3.57e+13 ohm | IEC 60093 |
| Dielectric Strength | 16.8 kV/mm @Thickness 2.00 mm |
427 kV/in @Thickness 0.0787 in |
IEC 60243-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Middle Barrel Temperature | 220 - 250 °C | 428 - 482 °F | |
| Front Barrel Temperature | 220 - 250 °C | 428 - 482 °F | |
| Nozzle Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| Injection Pressure | 30.0 - 100 MPa @Time 2.00 - 10.0 sec |
4350 - 14500 psi @Time 0.000556 - 0.00278 hour |
|
| Hold Pressure | 5.00 - 40.0 MPa @Time 10.0 - 30.0 sec |
725 - 5800 psi @Time 0.00278 - 0.00833 hour |
|
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm |
Users viewing this material also viewed the following:
- Nye Lubricants 760D (NG) Synthetic Oil
- Polymax® Maxelast® P3965H TPE, PP Overmold or Standalone use
- Honeywell PMP Polymethylpentene Film (discontinued **)
- Techmer ES Luriblend® PA6/6 CF33 ML2 BK 33% Carbon Filled
- A. Schulman POLYBATCH™ Blue 4300 Concentrate Based In Polyethylene
- A. Schulman POLYBATCH™ Yellow 20232U Concentrate Based In LLDPE
- A. Schulman POLYBATCH™ U-0294-L Blowing Agent Concentrate Based In PE
- Lushan PR320 Adhesive Resin for Aluminum Plastic Composite Pipe
- Bhansali Engineering Abstron IPM3000 PMMA- ABS Alloy
Copyright © lookpolymers.com All Rights Reserved