Ineos Styrenics 495F High-Impact Polystyrene Resin (Global)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Styrenics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Styrenics 495F High-Impact Polystyrene Resin (Global).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: High-impact, high-flow grade for a wide variety of applications, including appliance components, consumer electronics housings, magnetic and optical media, building and construction, packaging and food service, recreation equipment and sporting goods, medical devices and labware, office products, cosmetic and personal care products, and housewares.Information provided by BASF.Ineos Styrenics purchased this product line from BASF in 2005.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | <= 0.10 % | <= 0.10 % | 23°C/50% RH |
| Water Absorption at Saturation | <= 0.10 % | <= 0.10 % | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 55 | 55 | ASTM D785 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 55 % | 55 % | ASTM D638 |
| Tensile Modulus | 2.137 GPa | 310.0 ksi | ASTM D638 |
| Flexural Modulus | 1.655 GPa | 240.0 ksi | ASTM D790-1 |
| Izod Impact, Notched | 1.23 J/cm | 2.30 ft-lb/in | ASTM D256-A |
| Gardner Impact | 31.6 J @Thickness 3.17 mm, Temperature 23.0 °C |
23.3 ft-lb @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | ASTM D648 |
| Vicat Softening Point | 97.0 °C | 207 °F | ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.62 mm |
HB @Thickness 0.0638 in |
HB CSA 0.6, All Colors |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
HB UL94, All Colors |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 45 % | 45 % | 60°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 280 °C | 356 - 536 °F | Molding |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA - 51 UVT General Purpose Acrylic Resin
- RheTech Products RCC120-01 20% Calcium Carbonate Reinforced Polypropylene, Black, Recycled Content
- DuPont™ Clysar® LE Polyolefin Shrink Packaging Film, 75 Gauge (discontinued **)
- Indium Corp. 99.9% InI3 Indium Triiodide
- SPHERE ONE EXTENDOSPHERESâ„¢ XOL-150 Hollow Spheres
- CP-Polymer-Technik Wellamid® 6000 GV 30 HWCP 30% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- Chosun Refractories M55 Special High-Density Gunning Castable
- DuPont Teijin Films Melinex® FRP Polyester Film, 92 Gauge
- A. Schulman ComAlloy Hiloy® 112 Polypropylene, Glass Reinforced, Chemically Coupled, UL
- Lanxess Pocan® B 3215 000000 PBT, 10% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved