LG Chemical AF360C ABS, TBBA-free Flame Retardant, High Flow

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical AF360C ABS, TBBA-free Flame Retardant, High Flow.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Feature: Injection Molding, TBBA-free Flame Retardant, High FlowApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
<br>@Thickness 3.20 mm
 0.0040 - 0.0070 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 40 g/10 min
<br>@Load 10.0 kg,<br> Temperature 220 °C
 40 g/10 min
<br>@Load 22.0 lb,<br> Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 101
101
ASTM D785
Tensile Strength, Yield 39.2 MPa
<br>@Thickness 3.20 mm
 5690 psi
<br>@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 20 %
<br>@Thickness 3.20 mm
 20 %
<br>@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Yield >= 5.0 %
<br>@Thickness 3.20 mm
 >= 5.0 %
<br>@Thickness 0.126 in
 50 mm/min; ASTM D638
Tensile Modulus 2.26 GPa
<br>@Thickness 3.20 mm
 327 ksi
<br>@Thickness 0.126 in
 1 mm/min; ASTM D638
Flexural Yield Strength 68.6 MPa
<br>@Thickness 6.40 mm
 9960 psi
<br>@Thickness 0.252 in
 15 mm/min; ASTM D790
Flexural Modulus 2.40 GPa
<br>@Thickness 6.40 mm
 348 ksi
<br>@Thickness 0.252 in
 15 mm/min; ASTM D790
Izod Impact, Notched 1.67 J/cm
<br>@Thickness 6.40 mm,<br> Temperature 23.0 °C
 3.12 ft-lb/in
<br>@Thickness 0.252 in,<br> Temperature 73.4 °F
 ASTM D256
1.96 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 3.67 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 0.686 J/cm
<br>@Thickness 6.40 mm,<br> Temperature -30.0 °C
 1.29 ft-lb/in
<br>@Thickness 0.252 in,<br> Temperature -22.0 °F
 ASTM D256
0.686 J/cm
<br>@Thickness 3.20 mm,<br> Temperature -30.0 °C
 1.29 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
<br>@Thickness 6.40 mm
 190 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
<br>@Thickness 6.40 mm
 178 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 87.0 °C
<br>@Load 5.00 kg
 189 °F
<br>@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-0
<br>@Thickness >=1.50 mm
 V-0
<br>@Thickness >=0.0591 in
V-0
<br>@Thickness >=2.00 mm
 V-0
<br>@Thickness >=0.0787 in
V-0
<br>@Thickness >=3.00 mm
 V-0
<br>@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 170 - 190 °C
338 - 374 °F
Injection Molding
Middle Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Front Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Nozzle Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Back Pressure 0.490 - 0.981 MPa
71.1 - 142 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding