Overview of materials for Polyarylamide, Glass Fiber Filled

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyarylamide, Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyarylamide, Glass Fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.34 - 1.85 g/cc
0.0484 - 0.0668 lb/in³
Average value: 1.58 g/cc Grade Count:24
Filler Content 20.0 - 60.0 %
20.0 - 60.0 %
Average value: 42.2 % Grade Count:16
Water Absorption 0.100 - 0.220 %
0.100 - 0.220 %
Average value: 0.180 % Grade Count:11
Moisture Absorption at Equilibrium 1.11 - 2.00 %
1.11 - 2.00 %
Average value: 1.60 % Grade Count:10
Linear Mold Shrinkage 0.000500 - 0.00550 cm/cm
0.000500 - 0.00550 in/in
Average value: 0.00210 cm/cm Grade Count:21
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 70.0 - 269 MPa
10200 - 39000 psi
Average value: 189 MPa Grade Count:23
Elongation at Break 1.00 - 3.50 %
1.00 - 3.50 %
Average value: 2.06 % Grade Count:24
Modulus of Elasticity 6.50 - 26.0 GPa
943 - 3770 ksi
Average value: 15.6 GPa Grade Count:24
Flexural Yield Strength 120 - 390 MPa
17400 - 56500 psi
Average value: 278 MPa Grade Count:24
Flexural Modulus 5.50 - 24.0 GPa
798 - 3480 ksi
Average value: 14.9 GPa Grade Count:24
Izod Impact, Notched 0.350 - 1.30 J/cm
0.656 - 2.44 ft-lb/in
Average value: 0.771 J/cm Grade Count:23
Izod Impact, Unnotched 2.50 - 9.61 J/cm
4.68 - 18.0 ft-lb/in
Average value: 5.96 J/cm Grade Count:23
Thermal Properties Metric English Comments
CTE, linear 15.0 - 32.0 µm/m-°C
8.33 - 17.8 µin/in-°F
Average value: 21.4 µm/m-°C Grade Count:7
Thermal Conductivity 0.300 - 0.750 W/m-K
2.08 - 5.20 BTU-in/hr-ft²-°F
Average value: 0.430 W/m-K Grade Count:5
Melting Point 240 °C
464 °F
Average value: 240 °C Grade Count:10
Deflection Temperature at 1.8 MPa (264 psi) 135 - 241 °C
275 - 465 °F
Average value: 216 °C Grade Count:10
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:15
Oxygen Index 23.0 - 38.5 %
23.0 - 38.5 %
Average value: 27.1 % Grade Count:7
Electrical Properties Metric English Comments
Electrical Resistivity 3000 - 4.00e+15 ohm-cm
3000 - 4.00e+15 ohm-cm
Average value: 1.64e+15 ohm-cm Grade Count:7
Dielectric Constant 3.70 - 5.30
3.70 - 5.30
Average value: 4.28 Grade Count:6
Dielectric Strength 22.7 - 31.0 kV/mm
577 - 787 kV/in
Average value: 27.3 kV/mm Grade Count:6
Dissipation Factor 0.00700 - 0.0230
0.00700 - 0.0230
Average value: 0.0148 Grade Count:6
Arc Resistance 60.0 sec
60.0 sec
Average value: 60.0 sec Grade Count:3
Comparative Tracking Index 250 - 600 V
250 - 600 V
Average value: 474 V Grade Count:6
Processing Properties Metric English Comments
Melt Temperature 247 - 290 °C
477 - 554 °F
Average value: 269 °C Grade Count:24
Mold Temperature 120 - 141 °C
248 - 285 °F
Average value: 130 °C Grade Count:24
Drying Temperature 100 - 121 °C
212 - 250 °F
Average value: 119 °C Grade Count:14
Injection Pressure 50.0 - 250 MPa
7250 - 36300 psi
Average value: 127 MPa Grade Count:20