Quadrant EPP Cestlite™ ASTL Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | Quadrant Engineering Plastics Products |
| Trade Name | Cestlite™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quadrant EPP Cestlite™ ASTL Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Quadrant Engineering Plastic Products for polymers in their European product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ISO 1183 |
| Water Absorption | 0.050 % | 0.050 % | immersion |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 | 61 | after 15 sec.; ISO 868 |
| 63 | 63 | after 3 sec.; ISO 868 | |
| Ball Indentation Hardness | 37.0 MPa | 5370 psi | ISO 2039-1 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 |
| Elongation at Yield | 15 % | 15 % | ISO 527 |
| Tensile Modulus | 0.770 GPa | 112 ksi | ISO 527 |
| Compressive Yield Strength | 5.00 MPa | 725 psi | at 1% nominal strain; ISO 604 |
| 9.00 MPa | 1310 psi | at 2% nominal strain; ISO 604 | |
| 15.0 MPa | 2180 psi | at 5% nominal strain; ISO 604 | |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 8.00 J/cm² | 38.1 ft-lb/in² | Partial Break; ISO 179/1eA |
| Abrasion | 85 | 85 | Relative loss per DSM internal test (CESTILENE HD 1000 = 100) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 175 - 225 µm/m-°C @Temperature 20.0 °C |
97.2 - 125 µin/in-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | |
| Melting Point | 130 - 135 °C | 266 - 275 °F | ISO 3146; DSC, 10°C/min |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | 20,000 hours continuous |
| 120 °C | 248 °F | for short periods | |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ISO 75 method A |
| Vicat Softening Point | 83.0 °C | 181 °F | ISO 306 |
| Minimum Service Temperature, Air | -150 °C | -238 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | <= 20 % | <= 20 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | <= 1.00e+6 ohm-cm | <= 1.00e+6 ohm-cm | IEC 93 |
| Surface Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | IEC 93 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Omnia Plastica Omniamid PA6 G - G - at 50% RH
- NanoAmor 99%, OD/L: 40-60 nm/1-2 um Multi-Walled Carbon Nanotubes
- Huntsman IROGRAN® A 98 P 4535 TPU-Polyether
- LG Chemical Lupox® TE5011M PBT+PC
- ExxonMobil 3 Mobilith AW Series
- China Tungsten YG6A Tungsten Carbide for Cutting Tools
- A. Schulman ComAlloy Voloy® 688 Nylon 6/6, Glass Fiber/Bead Reinforced, Nylon 6/6 Alloy, Flame Retardant, UL
- 3M Scotch® 13 Electrical Semi-Conducting Tape
- Americas Styrenics STYRON® 487 High Impact Polystyrene
Copyright © lookpolymers.com All Rights Reserved