Radici Radilon® S RV250 (dry) Nylon 6

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	Radici Group Plastics
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Radici Radilon® S RV250 (dry) Nylon 6.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.

Physical Properties	Metric	English	Comments
Specific Gravity	1.30 g/cc	1.30 g/cc
Water Absorption	7.5 %	7.5 %
Moisture Absorption at Equilibrium	2.2 %	2.2 %
Viscosity Measurement	145	145	cm³/g Viscosity Number

Mechanical Properties	Metric	English
Tensile Strength at Break	155 MPa	22500 psi
Elongation at Break	4.1 %	4.1 %
Tensile Modulus	8.35 GPa	1210 ksi
Charpy Impact Unnotched	6.50 J/cm² <br>@Temperature -30.0 °C	30.9 ft-lb/in² <br>@Temperature -22.0 °F
	7.50 J/cm² <br>@Temperature 23.0 °C	35.7 ft-lb/in² <br>@Temperature 73.4 °F
Charpy Impact, Notched	1.10 J/cm² <br>@Temperature -30.0 °C	5.23 ft-lb/in² <br>@Temperature -22.0 °F
	1.30 J/cm² <br>@Temperature 23.0 °C	6.19 ft-lb/in² <br>@Temperature 73.4 °F

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F
Deflection Temperature at 0.46 MPa (66 psi)	205 °C	401 °F
Deflection Temperature at 1.8 MPa (264 psi)	195 °C	383 °F
Vicat Softening Point	210 °C <br>@Load 5.10 kg	410 °F <br>@Load 11.2 lb	50°C/h
Flammability, UL94	HB <br>@Thickness 1.60 mm	HB <br>@Thickness 0.0630 in
	HB <br>@Thickness 0.800 mm	HB <br>@Thickness 0.0315 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+11 ohm-cm	>= 1.00e+11 ohm-cm