Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
ExxonMobil LD 135.09 Cast Packaging Film Resin
(discontinued **) LD 135.09 is a homopolymer film resin with good clarity. It is suitable for processing in cast film equipment. Applications include food packaging, light to medium duty bags, and textile packaging.. |
|||
Film Tensile Strength at Break, TD | 17.9 - 251 MPa | 2600 - 36400 psi | Average value: 49.4 MPa Grade Count:113 |
Overview of materials for High Density Polyethylene (HDPE), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Film Grade". Each property range of values reported is minimum and max.. |
|||
Film Tensile Strength at Break, TD | 17.9 - 62.1 MPa | 2600 - 9000 psi | Average value: 39.2 MPa Grade Count:15 |
Overview of materials for Polychlorotrifluoroethylene; Molded This property data is a summary of similar materials in the MatWeb database for the category "Polychlorotrifluoroethylene; Molded". Each property range of values reported is minimum and maximum valu.. |
|||
Film Tensile Strength at Break, TD | 17.9 - 20.0 MPa | 2600 - 2900 psi | ASTM D882 |
Honeywell ACLAR® CX 130E Heat Sealable PCTFE Film
(discontinued **) Description: ACLAR® CX 130E is a heat sealable PCTFE film with outstanding clarity. It is used where applications require moisture protection.Information provided by Honeywell. |
|||
Film Tensile Strength at Break, TD | 17.9 - 20.0 MPa | 2600 - 2900 psi | ASTM D882 |
Honeywell ACLAR® Cx™ 8A Heat Sealable, Co-Extruded CTFE Film
(discontinued **) Description: ACLAR® Cx™ 8A is a heat sealable coextruded CTFE film.Information provided by Honeywell. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
LyondellBasell Petrothene® NA967000 Low Density Polyethylene, Film Extrusion Grade Petrothene NA967000 is a low density polyethylene resin designed for blown film, general purpose and industrial packaging applications. NA967000 exhibits good processing characteristics and impact s.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
Westlake EB169 Low Density Polyethylene Westlake EB169 is a low-density polyethylene with high stiffness designed for beverage shrink overwrap and towel/tissue packaging. It has good toughness and blends well with LLDPE resins.Application.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa @Thickness 0.0254 mm |
2600 psi @Thickness 0.00100 in |
ASTM D882A |
Total 9458 HDPE Film Grade Medium molecular weight grade. Excellent bubble stability, good compatibility with LDPE and LLDPE, good heat resistance, high stiffness and tensile strength.Applications: Release liners, Stand-up ba.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
Westlake EF606 Low Density Polyethylene Westlake EF606 is a LDPE resin suggested for use in multiwall and general purpose liners, and for use as a blend resin in general purpose packaging applications. It has excellent processability, and.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
Westlake Elevate™ EF545 4% Ethylene Vinyl Acetate Copolymer Westlake EF545 resin is a 4% EVA copolymer designed for films that require excellent optical and strength properties. This Kosher compliant resin has excellent heat sealing characteristics and low t.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
Chevron Phillips MarFlex® 9656 HDPE Blown Film Resin Resin Type: high density, linear polyethylene.Characteristics: copolymerization enhances film toughness, good drawdown, density level gives good machinability, blend well with LLDPEApplications: not.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
ExxonMobil LD 117.85 Blown Overwrap Film Resin Product Description: LD 117.85 is a homopolymer film resin with good clarity and excellent stiffness. Film made from LD 117.85 resin can be used in overwrap applications and in push-through type pac.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
ExxonMobil LDPE LD 117.85 Low Density Polyethylene Resin Product Description: LD 117.85 is a homopolymer film resin with good clarity and excellent stiffness. Film made from LD 117.85 resin can be used in overwrap applications and in push-through type pac.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
ExxonMobil LDPE LGA 105 Low Density Polyethylene Resin Product Description: LGA 105 is a homopolymer, garment film resin with good toughness. It is capable of being draw-down to thin gauges.Availability: North America Additive: Antiblock: NoSlip: NoPro.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | |
Dow LDPE 133A Low Density Polyethylene, Blown Film Grade DOW LDPE 133A resin is used for heavy duty blown film applications such as shrink film, shipping sacks, construction film, and other thick gauge film applications. It contains medium levels of antib.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | |
Dow LDPE 135A Low Density Polyethylene, Blown Film Grade DOW LDPE 135A resin is used for heavy duty blown film applications such as shrink film, shipping sacks, construction film, and other thick gauge film applications. It contains medium levels of slip .. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | |
Dow LDPE 170A Low Density Polyethylene, Blown Film Grade DOW LDPE 170A resin is used for shrink and heavy duty blown film applications where optical clarity is desired. It contains medium level of antiblock additives. It complies with U.S. FDA regulation .. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | |
Dow LDPE 640I Low Density Polyethylene, Liner Film Grade DOW LDPE 640I resin is a barefoot general purpose liner film resin for thin gauge applications requiring good drawdown and excellent toughness. This material complies with U.S.FDA regulation 21 CFR .. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | |
Dow LDPE 132I Low Density Polyethylene, Blown Film Grade DOW LDPE 132I is a barefoot resin for heavy duty blown film applications such as shrink film, shipping sacks, construction film, and other thick gauge film applications. It complies with U.S. FDA re.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D882 |
Dow XU 66129.00 Developmental Monolayer Adhesive Film XU 66129.00 Developmental Monolayer Adhesive Film is a heat-activated, thermally stable adhesive film capable of bonding to urethane foam-backed fabrics, paper, fiberglass, non-wovens, and rigid ure.. |
|||
Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | ASTM D-882 |
Bapolene® 200F Polyethylene, Film Grade Bapolene LD200F is a general purpose low density polyethylene for blown film extrusion applications. It contains medium levels of slip/antiblock additives. This product meets FDA standards for foo.. |