Total 9458 HDPE Film Grade

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer Total Atofina
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total 9458 HDPE Film Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium molecular weight grade. Excellent bubble stability, good compatibility with LDPE and LLDPE, good heat resistance, high stiffness and tensile strength.Applications: Release liners, Stand-up bags, Coextruded films, Shipping sacks, Multi-walled liners, Oriented film structures, Specialty packaging.Information provided provided by Total Petrochemicals.
Physical Properties Metric English Comments
Density 0.958 g/cc
0.0346 lb/in³
ASTM D792
Water Vapor Transmission 10.9 g/m²/day

@Thickness 0.0254 mm
 0.702 g/100 in²/day

@Thickness 0.00100 in
 ASTM F1249
Thickness 25.4 microns
1.00 mil
as tested; 2.5 BUR
Melt Flow 0.45 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 0.45 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 31.0 MPa

@Thickness 0.0254 mm
 4500 psi

@Thickness 0.00100 in
 ASTM D882A
Film Tensile Strength at Yield, TD 17.9 MPa

@Thickness 0.0254 mm
 2600 psi

@Thickness 0.00100 in
 ASTM D882A
Film Elongation at Break, MD 270 %

@Thickness 0.0254 mm
 270 %

@Thickness 0.00100 in
 ASTM D882A
Film Elongation at Break, TD <= 10 %

@Thickness 0.0254 mm
 <= 10 %

@Thickness 0.00100 in
 ASTM D882A
Elmendorf Tear Strength MD 15 g

@Thickness 0.0254 mm
 15 g

@Thickness 0.00100 in
 ASTM D1922
Elmendorf Tear Strength TD 1050 g

@Thickness 0.0254 mm
 1050 g

@Thickness 0.00100 in
 ASTM D1922
Dart Drop <= 1.97 g/micron

@Thickness 0.0254 mm
 <= 50.0 g/mil

@Thickness 0.00100 in
 ASTM D1709A
Dart Drop Test <= 50.0 g
<= 0.110 lb
1.0 mil; ASTM D1709A
Film Tensile Strength at Break, MD 53.1 MPa

@Thickness 0.0254 mm
 7700 psi

@Thickness 0.00100 in
 ASTM D882A
Film Tensile Strength at Break, TD 17.9 MPa

@Thickness 0.0254 mm
 2600 psi

@Thickness 0.00100 in
 ASTM D882A
1% Secant Modulus, MD 1050 MPa

@Thickness 0.0254 mm
 152000 psi

@Thickness 0.00100 in
 ASTM D882A
1% Secant Modulus, TD 1370 MPa

@Thickness 0.0254 mm
 199000 psi

@Thickness 0.00100 in
 ASTM D882A
Processing Properties Metric English Comments
Melt Temperature 193 - 216 °C
380 - 420 °F
Extrusion
Descriptive Properties Value Comments
Process Film
Region US & Canada