Polymer Property : Tensile Strength, Ultimate = 15200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	55.0 - 105 MPa @Temperature 60.0 - 150 °C	7980 - 15200 psi @Temperature 140 - 302 °F	Average value: 59.8 MPa Grade Count:3
Overview of materials for Polyphthalamide (PPA), 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are..
Tensile Strength, Ultimate	62.1 - 105 MPa	9000 - 15200 psi	Average value: 80.6 MPa Grade Count:8
Overview of materials for Polycarbonate/PET Polyester Blend, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/PET Polyester Blend, Glass Reinforced". Each property range of values reported is minimum ..
Tensile Strength, Ultimate	10.0 - 105 MPa @Temperature 60.0 - 150 °C	1450 - 15200 psi @Temperature 140 - 302 °F	Average value: 50.2 MPa Grade Count:6
Overview of materials for Nylon 6, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and max..
Tensile Strength, Ultimate	38.0 - 105 MPa	5510 - 15200 psi	Average value: 70.9 MPa Grade Count:17
Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ..
Tensile Strength, Ultimate	60.0 - 105 MPa	8700 - 15200 psi	Average value: 84.8 MPa Grade Count:3
Overview of materials for Nylon 66/6, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are incl..
Tensile Strength, Ultimate	90.0 - 105 MPa @Temperature 130 - 175 °C	13100 - 15200 psi @Temperature 266 - 347 °F	Average value: 88.6 MPa Grade Count:5
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. ..
Tensile Strength, Ultimate	90.0 - 105 MPa @Time 1.80e+7 - 7.20e+7 sec	13100 - 15200 psi @Time 5000 - 20000 hour	Average value: 88.6 MPa Grade Count:5
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. ..
Tensile Strength, Ultimate	47.0 - 105 MPa	6820 - 15200 psi	Average value: 80.2 MPa Grade Count:72
Overview of materials for Nylon 66, 40% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Mineral Filled". Specific grades with primary filler content between 35% and 44% are inclu..
Tensile Strength, Ultimate	45.0 - 105 MPa	6530 - 15200 psi	Average value: 69.6 MPa Grade Count:8
Overview of materials for Nylon 66/6, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, Mineral Reinforced". Each property range of values reported is minimum and maximum values of..
Tensile Strength, Ultimate	13.0 - 105 MPa	1890 - 15200 psi	Average value: 28.7 MPa Grade Count:73
Overview of materials for Polypropylene with 10% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Talc Filler". Specific grades with primary filler content between 5% and 14% are ..
Tensile Strength, Ultimate	45.0 - 105 MPa	6530 - 15200 psi	Average value: 57.6 MPa Grade Count:21
Overview of materials for Polybutylene Terephthalate (PBT), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Mineral Filled". Each property range of values reported is minimum and..
Tensile Strength, Ultimate	75.0 - 105 MPa	10900 - 15200 psi	ASTM D638-68
Budd DSM-949, Diesel Grade SMC, Vinyl Ester, Black (discontinued **) Used for parts requiring high strength at room temperature, good retention of properties at high temperatures and corrosion resistance, such as diesel engine external body parts.Data provided by the..