Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and .. |
|||
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
Injection; ISO 11359-2 |
Raschig Group 2572 AMC Glass fiber reinforced Polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance in combin.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | Below glass transition temp; ASTM D696 |
Performance Polymers IPS II PPL-C4250 PEKK (Polyetherketoneketone) Linear 30% Carbon Fiber Reinforced Molding Grade Black pelletsInformation provided by Infinite Polymer System II. |
|||
CTE, linear | 10.0 - 14.0 µm/m-°C @Temperature -40.0 - 125 °C |
5.56 - 7.78 µin/in-°F @Temperature -40.0 - 257 °F |
X/Y; IPC-TM-650.2.4.41 |
Park Electrochemical Nelco® N4380-13 RF Microwave Performance, Modified Epoxy The Nelco N4350-13 RF and N4380-13 RF series are enhanced epoxy resin systems specifically engineered to provide a unique solution for design applications that demand outstanding thermal properties,.. |
|||
CTE, linear | 10.0 - 20.0 µm/m-°C @Temperature 50.0 - 100 °C |
5.56 - 11.1 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group RALUPOL® 8602 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng.. |
|||
CTE, linear | 10.0 - 50.0 µm/m-°C | 5.56 - 27.8 µin/in-°F | Average value: 25.9 µm/m-°C Grade Count:27 |
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
CTE, linear | 10.0 - 30.0 µm/m-°C | 5.56 - 16.7 µin/in-°F | Average value: 19.6 µm/m-°C Grade Count:26 |
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl.. |
|||
CTE, linear | 10.0 - 100 µm/m-°C | 5.56 - 55.6 µin/in-°F | Average value: 63.3 µm/m-°C Grade Count:8 |
Overview of materials for Nylon 66, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Extruded". Each property range of values reported is minimum and maximum values of appropriate.. |
|||
CTE, linear | 10.0 - 27.0 µm/m-°C | 5.56 - 15.0 µin/in-°F | Average value: 20.5 µm/m-°C Grade Count:25 |
Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. .. |
|||
CTE, linear | 10.0 - 500 µm/m-°C | 5.56 - 278 µin/in-°F | Average value: 55.8 µm/m-°C Grade Count:37 |
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of.. |
|||
CTE, linear | 10.0 - 500 µm/m-°C | 5.56 - 278 µin/in-°F | Average value: 70.1 µm/m-°C Grade Count:46 |
Overview of materials for Nylon 612, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Glass Fiber Filler". Each property range of values reported is minimum and maximum values of .. |
|||
CTE, linear | 10.0 - 37.8 µm/m-°C | 5.56 - 21.0 µin/in-°F | Average value: 16.3 µm/m-°C Grade Count:21 |
Overview of materials for Nylon 12, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
CTE, linear | 10.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C |
5.56 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F |
x-axis; IPC-TM 650-2.4.24 |
Industrial Laminates/Norplex NP344 Cotton Fabric Description: Fine weave canvas laminate with high temperature phenolic resin and molybdenum disulfide lubricant. Good machining properties and low coefficient of thermal expansion. Better machining .. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® BMC 0180 Unsaturated Polyester UP BMC 0180 is a general purpose BMC for electrical applications. Product according to type 803 DIN 16911. The glass content is on a level that combines good mould ability with good strength and stiffn.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® SMC 0390 Unsaturated Polyester UP SMC 0390 is a standard low profile SMC. Because of its low shrinkage, the material shows good surface quality as well as very low warpage. The product is suitable for applications if a better surfac.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Menzolit Menzolit® SMC 0430 Unsaturated Polyester UP SMC 0430 is a low emission Class-A SMC for on-line painted exterior body applications on passenger cars. These compounds mould to parts with excellent surface quality for on-line painted body panel.. |
|||
CTE, linear | 10.0 - 12.0 µm/m-°C @Temperature 20.0 °C |
5.56 - 6.67 µin/in-°F @Temperature 68.0 °F |
|
MMCC Al/SiC 3DP Particulate Aluminum Matrix Composite Cast, discontinuously reinforced aluminum matrix composite. May be fabricated by vacuum infiltration of the ceramic preform.Data provided by the manufacturer, Metal Matrix Cast Composites (MMCC). |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | (z) |
GrafTech GRAFCELL® FFP-100 SERIES Flow Field Plate Graphite Manufactured from expanded natural graphite, GRAFCELL® Flow Field Plate (FFP) components retain a continuous graphitic phase. This phase continuity, combined with a low contact resistance, provid.. |
|||
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | (z) |
GrafTech GRAFCELL® FFP-300 SERIES Flow Field Plate Graphite Manufactured from expanded natural graphite, GRAFCELL® Flow Field Plate (FFP) components retain a continuous graphitic phase. This phase continuity, combined with a low contact resistance, provid.. |
|||
CTE, linear | 10.0 µm/m-°C @Temperature 25.0 - 500 °C |
5.56 µin/in-°F @Temperature 77.0 - 932 °F |
|
Wieland Zeno™ Zr Disc Zirconium Oxide Zirconium oxide blanks supplied partly sintered. Available in five different thicknesses to reduce material costs. Applications: modern dental restorationsDental |
|||
CTE, linear | 10.0 - 13.0 µm/m-°C @Temperature 20.0 °C |
5.56 - 7.22 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance A-5S Alnico Magnetic Material |
|||
CTE, linear | 10.0 - 13.0 µm/m-°C @Temperature 20.0 °C |
5.56 - 7.22 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance A-8S Alnico Magnetic Material |
|||
CTE, linear | 10.0 - 30.0 µm/m-°C @Temperature 20.0 °C |
5.56 - 16.7 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance BCN-11 Bonded (Composite) Magnetic Material |
|||
CTE, linear | 10.0 µm/m-°C @Temperature 20.0 °C |
5.56 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance S-30B Samarium Cobalt Magnetic Material |
|||
CTE, linear | 10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
Ascend Performance Materials Vydyne® 20NSP Nylon 66, DAM Vydyne® 20NSP is a general-purpose, highly nucleated, lubricated PA66 resin available in natural color. It is designed to crystallize rapidly in order to reduce cycle times and increase productivit.. |
|||
CTE, linear | 10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
Ascend Performance Materials Vydyne® 65A Nylon 66, General Purpose, intermediate viscosity, DAM Vydyne® 65A is a medium-viscosity, heat-stabilized PA66 resin suitable for injection-molding extrusion and compounding applications. It is available in natural color only. Vydyne 65A resin offers h.. |
|||
CTE, linear | 10.0 - 30.0 µm/m-°C @Temperature 20.0 °C |
5.56 - 16.7 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance BCN-14 Bonded (Composite) Magnetic Material |
|||
CTE, linear | 10.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
5.56 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359-2 |
Ascend Performance Materials Vydyne® 67B Nylon 66, General Purpose, very high viscosity, DAM Vydyne® 67B is a very-high-viscosity PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 67B resin offers high strength, rigidity and.. |
|||
CTE, linear | 10.0 - 100 µm/m-°C @Temperature -100 - 250 °C |
5.56 - 55.6 µin/in-°F @Temperature -148 - 482 °F |
Average value: 21.2 µm/m-°C Grade Count:23 |
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS)- 40% Glass filled; Molded". Specific grades with glass content between 35% a.. |