Arlon R31310R012 Uncured Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon R31310R012 Uncured Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Aluminized PET FilmSide 2: Uncured Rubber This data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Thickness 25.4 microns
1.00 mil
Side 1
38.1 microns
1.50 mil
Polyethylene, Interleave
>= 102 microns
>= 4.00 mil
Side 2
178 microns
7.00 mil
Prime Coated 1628 Fiberglass, Substrate
Mechanical Properties Metric English Comments
Hardness, Shore A 40 - 50
40 - 50
Compound Property
Tensile Strength 5.58 - 6.83 MPa
810 - 990 psi
Compound Property
Elongation at Break 450 - 550 %
450 - 550 %
Compound Property
Peel Strength >= 0.877 kN/m
>= 5.00 pli
Bond Strength (Rubber to Rubber)
>= 0.877 kN/m
>= 5.00 pli
Bond Strength (Rubber to Polyester)
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 204 °C
400 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Electrical Properties Metric English Comments
Dielectric Strength >= 15.7 kV/mm
>= 400 kV/in
Processing Properties Metric English Comments
Cure Time 15.0 min

@Pressure 0.345 MPa,
Temperature 177 °C
0.250 hour

@Pressure 50.0 psi,
Temperature 350 °F
Recommended Cure Cycle
Descriptive Properties Value Comments
Color Red
Side 2
Silver
Side 1
Total Product Weight (oz/yd2) 12 - 14
Uncoated Fabric Break Strength 200 lb/in
Fill Direction, Substrate Property
250 lb/in
Warp Direction, Substrate Property