BASF Ultradur B 4040 G10 High Speed BK15029 50% Glass Filled PBT/PET

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET)
Manufacturer BASF
Trade Name Ultradur B
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur B 4040 G10 High Speed BK15029 50% Glass Filled PBT/PET.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultradur B 4040 G10 High Speed BK15029 is a high flow, fast cycling with low warpage, 50% glass filled, injection molding PBT for industrial parts, rigid tough and dimensional stable applications.
Physical Properties Metric English Comments
Density 1.76 g/cc
0.0636 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
ISO 62
Moisture Absorption at Equilibrium 0.12 %
0.12 %
23°C/50% R.H.; ISO 62
Viscosity Test 75 cm³/g
75 cm³/g
Viscosity number
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO Data
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO Data
Melt Flow 130 g/10 min

@Load 2.16 kg,
Temperature 275 °C
130 g/10 min

@Load 4.76 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 150 MPa
21800 psi
5mm/min; ISO 527
Elongation at Break 1.2 %
1.2 %
5mm/min; ISO 527
Tensile Modulus 18.4 GPa
2670 ksi
1mm/min; ISO 527
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C
13.9 µin/in-°F
ISO 11359
Melting Point 223 °C
433 °F
10 K/min
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 4.5

@Frequency 1.00e+6 Hz
4.5

@Frequency 1.00e+6 Hz
IEC 60250
4.7

@Frequency 100 Hz
4.7

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.0020

@Frequency 100 Hz
0.0020

@Frequency 100 Hz
IEC 60250
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 225 V
225 V
IEC 60112
Descriptive Properties Value Comments
Color BK15029
Commercial Status North America and Europe
Impact Modified No
Primary Processing Technique Injection Molding