BASF Ultramid® B3EG3 15% Glass Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3EG3 15% Glass Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 15% glass-fiber reinforced injection-molding grade with enhanced impact resistance, for example, for vehicle mirror housings as well as for the wheels of mountain bikes.Information provided by BASF
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 7.7 - 8.3 %
7.7 - 8.3 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 2.3 %
2.3 %
50% RH
2.3 - 2.9 %
2.3 - 2.9 %
23°C; 50% RH; ISO 62
7.7 %
7.7 %
Saturation
Viscosity Measurement 140
140
ISO 307
Linear Mold Shrinkage 0.0045 cm/cm
0.0045 in/in
restricted
Melt Flow 92.25 g/10 min

@Load 5.00 kg,
Temperature 275 °C
92.25 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 70.0 MPa
10200 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 15 %
15 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 3.50 GPa
508 ksi
ISO 527-1/-2
Flexural Strength 100 MPa
14500 psi
at max force; ISO 178
Flexural Modulus 2.50 GPa
363 ksi
ISO 178
Charpy Impact Unnotched 10.5 J/cm²

@Temperature 23.0 °C
50.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 2100 MPa

@Strain <=0.500 %
305000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
Specific Heat Capacity 1.60 J/g-°C
0.382 BTU/lb-°F
Thermal Conductivity 0.340 W/m-K
2.36 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 135 °C
275 °F
for 50% loss of tensile strength after 20000hr
165 °C
329 °F
for 50% loss of tensile strength after 5000hr
200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
ISO 75-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093
Dielectric Constant 7.0

@Frequency 1.00 Hz
7.0

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.24

@Frequency 1.00e+6 Hz
0.24

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 550 V
550 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Descriptive Properties Value Comments
Commercial Status Europe and North America