Borealis Xmod™ BG055AI High Stiffness Polypropylene for Injection Molding Applications

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer Borealis
Trade Name Xmod™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Xmod™ BG055AI High Stiffness Polypropylene for Injection Molding Applications.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xmod BG055AI is a high melt flow polypropylene with increased crystallinity, intended for injection molding. Xmod BG055AI is a very easy flowing material with a good balance between impact strength and stiffness. The material provides high surface quality.Xmod BG055AI is especially designed for air duct systems, climate control units, back-injection molding, and parts requiring high aesthetic surface finish.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ISO 1183
Melt Flow 22 g/10 min

@Load 2.16 kg,
Temperature 230 °C
22 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
96 g/10 min

@Load 5.00 kg,
Temperature 230 °C
96 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 85.0 MPa
12300 psi
H 385/30; ISO 2039
Tensile Strength, Yield 35.0 MPa
5080 psi
At 50 mm/min; ISO 527-2
Tensile Modulus 2.00 GPa
290 ksi
At 1 mm/min; ISO 527-2
Flexural Modulus 1.85 GPa
268 ksi
At 2 mm/min; ISO 178
Charpy Impact Unnotched 10.2 J/cm²
48.5 ft-lb/in²
ISO 179/1eU
3.50 J/cm²

@Temperature -20.0 °C
16.7 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179/1eA
0.150 J/cm²

@Temperature -20.0 °C
0.714 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 108 °C
226 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75-2
Vicat Softening Point 95.0 °C
203 °F
B (50N); ISO 306
156 °C
313 °F
A (10N); ISO 306
Shrinkage 1.5 %

@Thickness 2.00 mm
1.5 %

@Thickness 0.0787 in
disk; Borealis Method
Optical Properties Metric English Comments
Gloss 75 %
75 %
20°; DIN 67530
95 %
95 %
60°; DIN 67530
Processing Properties Metric English Comments
Melt Temperature 210 - 260 °C
410 - 500 °F
Polymer Mass Temp
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Descriptive Properties Value Comments
Emissions, ug C/g 30
VDA 277
Fogging, mg 1.1
At 100°C/ 16 hours