Chevron Phillips HiD® 9638 HDPE Sheeting and Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips HiD® 9638 HDPE Sheeting and Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: Sheeting Resin for the Geomembrane Market; ASTM D 4976 Classification: PE 225, A 56507Applications:Cast Geomembrane Applications, Notion and Millinery Bags, Heavy Duty Shipping Sacks, Insulation Bags, Multi-Wall Liners, Coextruded Film StructuresFilm properties below based on film thickness of 20 µm.Data provided by Chevron Chemical.
Physical Properties Metric English Comments
Density 0.939 g/cc
0.0339 lb/in³
ASTM D1505
Environmental Stress Crack Resistance >= 2000 hour

@Temperature 50.0 °C
>= 2000 hour

@Temperature 122 °F
F<sub>50</sub>, Cond. B.; ASTM D1693
Melt Flow 0.25 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.25 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
High Load Melt Index 21 g/10 min

@Load 21.6 kg,
Temperature 190 °C
21 g/10 min

@Load 47.6 lb,
Temperature 374 °F
High Load Melt Index; ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 31.0 MPa
4500 psi
ASTM D638
Tensile Strength, Yield 21.0 MPa
3050 psi
ASTM D638
Film Elongation at Break, MD 370 %
370 %
ASTM D882
580 %
580 %
ASTM D882
Elongation at Break >= 800 %
>= 800 %
Molded; ASTM D638
Flexural Modulus 0.660 GPa
95.7 ksi
3 pt. secant. ASTM D790
Secant Modulus, MD 0.410 GPa
59.5 ksi
ASTM D882
Secant Modulus, TD 0.480 GPa
69.6 ksi
ASTM D882
Elmendorf Tear Strength, MD 1.18 g/micron
30.0 g/mil
Notched; ASTM D1922
Elmendorf Tear Strength, TD 27.2 g/micron
690 g/mil
ASTM D1922
Dart Drop 7.50 g/micron
191 g/mil
F<sub>50</sub>; 1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD 48.0 MPa
6960 psi
ASTM D882
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 121 °C
250 °F
ASTM D1525
Brittleness Temperature <= -59.0 °C
<= -74.2 °F
ASTM D746