DSM Arnite® TV4 260 SF PBT-30% Glass Reinforced (European and Asian Grade)  (discontinued **)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Arnite® TV4 260 SF PBT-30% Glass Reinforced (European and Asian Grade)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame retardant gradesEasy molding FR grades for connectorsToughened unfilled materials for durabilityHigh modulus, tight specification for critical auto componentsToughened reinforced resinsLow outgassing grades for reflector surfacesArnite extrusion resins: Specialized materials for specific usesPET for medical applicationsLoose buffer Optical fiber tubingPET for stock shapesApplicationsAutomotive:Connectors, sensors and E&E parts, Exterior fittings, Gear housings and motors, Brake valve bodiesElectrical & Electronic: Telecoms and IT connectors, Bobbins, Low voltage Power distribution, E-motor components, Lightings and Lamp fittingsConsumer Durables: Small AppliancesOther: Optical fiber tubingInformation provided by DSM.
Physical Properties Metric English Comments
Density 1.65 g/cc
0.0596 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
Sim. to ISO 62
Moisture Absorption at Equilibrium 0.15 %
0.15 %
Humidity Absorption; Sim. to ISO 62
Melt Flow 13.2 g/10 min

@Load 2.16 kg,
Temperature 250 °C
13.2 g/10 min

@Load 4.76 lb,
Temperature 482 °F
Calculated from Volume Flow Rate of 8 cm<sup>3</sup>/10min.; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
ISO 527-1/-2
Elongation at Break 2.5 %
2.5 %
ISO 527-1/-2
Tensile Modulus 11.0 GPa
1600 ksi
ISO 527-1/-2
Charpy Impact Unnotched 5.00 J/cm²

@Temperature -30.0 °C
23.8 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.800 J/cm²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature 20.0 °C
22.2 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/-2
UL RTI, Electrical 140 °C

@Thickness 1.50 mm
284 °F

@Thickness 0.0591 in
UL746B
140 °C

@Thickness 0.750 mm
284 °F

@Thickness 0.0295 in
UL746B
UL RTI, Mechanical with Impact 150 °C

@Thickness 0.750 mm
302 °F

@Thickness 0.0295 in
UL746B
150 °C

@Thickness 1.50 mm
302 °F

@Thickness 0.0591 in
UL746B
UL RTI, Mechanical without Impact 140 °C

@Thickness 1.50 mm
284 °F

@Thickness 0.0591 in
UL746B
140 °C

@Thickness 0.750 mm
284 °F

@Thickness 0.0295 in
UL746B
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
IEC 60695-11-10
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
IEC 60695-11-10
Glow Wire Test 725 °C

@Thickness 1.50 mm
1340 °F

@Thickness 0.0591 in
Glow Wire Ignition Temperature; IEC 60695-2-13
800 °C

@Thickness 0.750 mm
1470 °F

@Thickness 0.0295 in
Glow Wire Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 0.750 mm
1760 °F

@Thickness 0.0295 in
Glow Wire Flammability Index; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.8

@Frequency 1e+6 Hz
3.8

@Frequency 1e+6 Hz
IEC 60250
4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 28.0 kV/mm
711 kV/in
IEC 60243-1
Dissipation Factor 0.0025

@Frequency 100 Hz
0.0025

@Frequency 100 Hz
IEC 60250
0.014

@Frequency 1e+6 Hz
0.014

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 300 V
300 V
IEC 60112
250 - 399 V
250 - 399 V
PLC 2; UL 746A
Descriptive Properties Value Comments
Flame Retardant Yes
Flame Retarding Agent Yes
Injection molding Yes
Release Agent Yes
With Fillers Yes