DuPont Performance Polymers Delrin® 510GR NC000 Acetal (POM) (Unverified Data**)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Glass Fiber Reinforced
Manufacturer	DuPont Performance Polymers
Trade Name	Delrin®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Delrin® 510GR NC000 Acetal (POM) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

10% Glass Reinforced Medium Viscosity Acetal Homopolymer Delrin 510GR is a 10% glass reinforced acetal homopolymer for injection molding. It has high strength stiffness and high deflection temperature and excellent creep resistance.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.49 g/cc	0.0538 lb/in³	ISO 1183
Water Absorption	1.1 % @Thickness 2.00 mm	1.1 % @Thickness 0.0787 in	Sim. to ISO 62
Moisture Absorption	0.160 % @Thickness 2.00 mm	0.160 % @Thickness 0.0787 in	Sim. to ISO 62
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.014 cm/cm	0.014 in/in	ISO 294-4 2577
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 190 °C	12 g/10 min @Load 4.76 lb, Temperature 374 °F	cm³/10min; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	95.0 MPa	13800 psi	ISO 527-1/-2
Tensile Stress	7.325 MPa @Strain 0.100 %, Temperature 23.0 °C	1062 psi @Strain 0.100 %, Temperature 73.4 °F	ISO 11403-1 -2
	38.14 MPa @Strain 0.700 %, Temperature 23.0 °C	5531 psi @Strain 0.700 %, Temperature 73.4 °F	ISO 11403-1 -2
	58.68 MPa @Strain 1.20 %, Temperature 23.0 °C	8511 psi @Strain 1.20 %, Temperature 73.4 °F	ISO 11403-1 -2
	74.43 MPa @Strain 1.70 %, Temperature 23.0 °C	10800 psi @Strain 1.70 %, Temperature 73.4 °F	ISO 11403-1 -2
	108.0 MPa @Strain 3.40 %, Temperature 23.0 °C	15660 psi @Strain 3.40 %, Temperature 73.4 °F	ISO 11403-1 -2
Elongation at Break	4.3 %	4.3 %	ISO 527-1/-2
Tensile Modulus	5.50 GPa	798 ksi	ISO 527-1/-2
Flexural Modulus	4.80 GPa	696 ksi	ISO 178
Secant Modulus	3.56 GPa @Strain 2.80 %, Temperature 23.0 °C	516 ksi @Strain 2.80 %, Temperature 73.4 °F	ISO 11403-1 -2
	4.04 GPa @Strain 2.10 %, Temperature 23.0 °C	586 ksi @Strain 2.10 %, Temperature 73.4 °F	ISO 11403-1 -2
	4.67 GPa @Strain 1.40 %, Temperature 23.0 °C	678 ksi @Strain 1.40 %, Temperature 73.4 °F	ISO 11403-1 -2
	5.45 GPa @Strain 0.700 %, Temperature 23.0 °C	790 ksi @Strain 0.700 %, Temperature 73.4 °F	ISO 11403-1 -2
	7.325 GPa @Strain 0.100 %, Temperature 23.0 °C	1062 ksi @Strain 0.100 %, Temperature 73.4 °F	ISO 11403-1 -2
Izod Impact, Notched (ISO)	5.00 kJ/m²	2.38 ft-lb/in²	ISO 180/1A
Charpy Impact Unnotched	5.00 J/cm²	23.8 ft-lb/in²	ISO 179/1eU
	5.00 J/cm² @Temperature -30.0 °C	23.8 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	ISO 179/1eA
	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
Tensile Creep Modulus, 1 hour	4800 MPa @Time 3600 sec	696000 psi @Time 1.00 hour	ISO 899-1
Tensile Creep Modulus, 1000 hours	3500 MPa @Time 3.60e+6 sec	508000 psi @Time 1000 hour	ISO 899-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	70.0 µm/m-°C	38.9 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C	55.6 µin/in-°F	ISO 11359-1/-2
Melting Point	178 °C	352 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	174 °C	345 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	164 °C	327 °F	ISO 75-1/-2
Vicat Softening Point	160 °C	320 °F	50°C/h 50N; ISO 306
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Dielectric Constant	3.7 @Frequency 100 Hz	3.7 @Frequency 100 Hz	IEC 60250
	3.9 @Frequency 1.00e+6 Hz	3.9 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Descriptive Properties	Value	Comments
Additives	Release agent
Delivery Form	Pellets
Part Marking Code	>POM-GF10<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	POM-GF-10	ISO 1043
UL recognition	UL