EMS-Grivory Grivory® FG 40 NL nat 6018 PA6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® FG 40 NL nat 6018 PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 9.0 % | 9.0 % | ISO 62 |
| Moisture Absorption | 3.00 % | 3.00 % | ISO 62 |
| Water Vapor Transmission | 10.0 g/m²/day | 0.644 g/100 in²/day | 23°C/85%r.h.; DIS 15106-1/-2 |
| Oxygen Transmission Rate | 25.0 cc/m²/day | 1.61 cc/100 in²/day | 23°C/0%r.h.; DIS 15105-1/-2 |
| 40.0 cc/m²/day | 2.58 cc/100 in²/day | 23°C/85%r.h.; DIS 15105-1/-2 | |
| Carbon Dioxide Transmission | 80.0 cc-mm/m²-24hr-atm | 203 cc-mil/100 in²-24hr-atm | 23°C/0%r.h.; DIS 15105-1/-2 |
| 200 cc-mm/m²-24hr-atm | 508 cc-mil/100 in²-24hr-atm | 23°C/85%r.h.; DIS 15105-1/-2 | |
| Melt Flow | 20 g/10 min | 20 g/10 min | (MVR) [cm³/10min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 40.0 MPa | 5800 psi | ISO 527-3 |
| Film Elongation at Break, MD | 600 % | 600 % | ISO 527-3 |
| Film Elongation at Break, TD | 900 % | 900 % | ISO 527-3 |
| Film Elongation at Yield, MD | 10 % | 10 % | ISO 527-3 |
| Film Elongation at Yield, TD | 7.0 % | 7.0 % | ISO 527-3 |
| Tensile Modulus | 1.10 GPa | 160 ksi | conditioned; ISO 527-1/-2 |
| 3.00 GPa | 435 ksi | dry; ISO 527-1/-2 | |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | ISO 8295 |
| Tear Strength | 50.0 kN/m | 285 pli | Trouser Tear resistance MD; ISO 6383-1 |
| 50.0 kN/m | 285 pli | Trouser Tear resistance TD; ISO 6383-1 | |
| Elmendorf Tear Strength MD | 1530 g | 1530 g | ISO 6383-2 |
| Elmendorf Tear Strength TD | 1530 g | 1530 g | ISO 6383-2 |
| Film Tensile Strength at Break, MD | 100 MPa | 14500 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 90.0 MPa | 13100 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 100 % | 100 % | 60°; ISO 2813 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Food contact | EU Requirements | |
| FDA | ||
| Form | Granules | |
| Gelboflextest [holes/m²], EMS | 800 | |
| Packaging | Medical packaging | |
| Non oriented film | ||
| Oriented film | ||
| Paper coating | ||
| Tubes | ||
| Processing | Blown Film Extrusion | |
| Film Extrusion | ||
| Other Extrusion | ||
| Product Attributes | Barrier Properties | |
| High viscosity | ||
| Nucleated |
Users viewing this material also viewed the following:
- Nyco M1250 AS WOLLASTOCOAT® Wollastonite
- Nabaltec ACTILOX® B30 AlO(OH) Boehmite
- Polykemi AB POLYplex PMMA 500 Acrylic Glass
- Qualchem Danamid AFGFS2HUV30 Polyamide 66, 30% Glass Fiber
- Solvay Specialty Polymers Primef® 7010 Polyphenylene Sulfide (PPS), 65% GlassMineral (discontinued **)
- Plastcom SLOVAMID 6 NG GF 20 HLS PA6, 20% glass fibre, combined stability
- Borealis MB250WG Polypropylene Compound, Mineral Filled
- Goodfellow Platinum 90/Rhodium 10 Thermocouple Alloy
- 3M XR8115 Double Coated Paper Tapes
- Saint-Gobain Chemfab® 1565V PTFE Coated Fiberglass Conveyor Belting
Copyright © lookpolymers.com All Rights Reserved