ExxonMobil Escorene® LD-102 LDPE Drawdown Resin, 1.25 mil Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-102 LDPE Drawdown Resin, 1.25 mil Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A homopolymer, good clarity, laundry and dry cleaning film resin capable of providing a tough film in very thin gauges.Applications: Dry cleaning establishment bags; Protective garment bags; Other film applications requiring drawdown to 0.5 mil or below. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 6.5 g/10 min
6.5 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 350 %
350 %
ASTM D882
Film Elongation at Break, TD 650 %
650 %
ASTM D882
Secant Modulus, MD 0.176 GPa
25.5 ksi
ASTM D882
Secant Modulus, TD 0.186 GPa
27.0 ksi
ASTM D882
Elmendorf Tear Strength MD 280 g
280 g
ASTM D1922
Elmendorf Tear Strength TD 210 g
210 g
ASTM D1922
Elmendorf Tear Strength, MD 8.82 g/micron
224 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 6.61 g/micron
168 g/mil
ASTM D1922
Dart Drop 2.68 g/micron
68.0 g/mil
F50; ASTM D1709
Dart Drop Test 85.0 g
0.187 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 19.0 MPa
2760 psi
ASTM D882
Film Tensile Strength at Break, TD 16.0 MPa
2320 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 110 °C
230 °F
Exxon Method
Optical Properties Metric English Comments
Haze 6.4 %
6.4 %
ASTM D1003
Gloss 71 %
71 %
45°, ASTM D-2457