ExxonMobil LDPE LD 185JD Low Density Polyethylene Resin (European Grade)

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 185JD Low Density Polyethylene Resin (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 185 series offer good optical properties and sealing characteristics. LD 185 is manufactured with narrow specifications to suit the high consistency requirements of lamination films.Availability: Africa & Middle East and Europe Additive: Antiblock: 1800 ppmSlip: 330 ppmThermal Stabilizer: YesApplications: Co-Extrusion FilmsDisplay Packaging FilmFood packagingForm Fill and Seal PackagingHigh Quality LaminationLamination FilmInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
ExxonMobil method
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 1800 ppm
1800 ppm
Slip Level 330 ppm
330 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 370 %
370 %
ASTM D882
Film Elongation at Break, TD 550 %
550 %
ASTM D882
Elmendorf Tear Strength MD 150 g
150 g
ASTM D1922
Elmendorf Tear Strength TD 110 g
110 g
ASTM D1922
Dart Drop Test 80.0 g
0.176 lb
ASTM D1709A
Film Tensile Strength at Break, MD 29.0 MPa
4200 psi
ASTM D882
Film Tensile Strength at Break, TD 22.8 MPa
3300 psi
ASTM D882
1% Secant Modulus, MD 207 MPa
30000 psi
ASTM D882
1% Secant Modulus, TD 241 MPa
35000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 230 °C
<= 446 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 6.3 %
6.3 %
ASTM D1003
Gloss 65 %
65 %
45°; ASTM D2457