Hexcel® HexPly® F593 Epoxy Resin, W3G282 Carbon Fabric

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F593 Epoxy Resin, W3G282 Carbon Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hexcel designation: W3G282-42"-F593; Fiber: Amoco T-300/3kInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 2.965 MPa

@Temperature 93.0 °C
 430.0 psi

@Temperature 199 °F
 Sandwich Flatwise Tension, Wet
3.896 MPa

@Temperature 93.0 °C
 565.1 psi

@Temperature 199 °F
 Sandwich Flatwise Tension, Dry
4.682 MPa

@Temperature -59.0 °C
 679.1 psi

@Temperature -74.2 °F
 Sandwich Flatwise Tension, Dry
4.806 MPa

@Temperature 24.0 °C
 697.1 psi

@Temperature 75.2 °F
 Sandwich Flatwise Tension, Dry
419 MPa

@Temperature 71.0 °C
 60800 psi

@Temperature 160 °F
 Wet
420 MPa

@Temperature 93.0 °C
 60900 psi

@Temperature 199 °F
 Dry
462 MPa

@Temperature 71.0 °C
 67000 psi

@Temperature 160 °F
 Dry
485 MPa

@Temperature -54.0 °C
 70300 psi

@Temperature -65.2 °F
 Dry
637 MPa

@Temperature 24.0 °C
 92400 psi

@Temperature 75.2 °F
 Dry
Tensile Modulus 49.6 GPa

@Temperature 71.0 °C
 7190 ksi

@Temperature 160 °F
 Wet
51.7 GPa

@Temperature 71.0 °C
 7500 ksi

@Temperature 160 °F
 Dry
53.8 GPa

@Temperature 93.0 °C
 7800 ksi

@Temperature 199 °F
 Dry
55.2 GPa

@Temperature -54.0 °C
 8010 ksi

@Temperature -65.2 °F
 Dry
56.5 GPa

@Temperature 24.0 °C
 8190 ksi

@Temperature 75.2 °F
 Dry
Compressive Yield Strength 410 MPa

@Temperature 71.0 °C
 59500 psi

@Temperature 160 °F
 Wet
469 MPa

@Temperature 93.0 °C
 68000 psi

@Temperature 199 °F
 Dry
536 MPa

@Temperature 71.0 °C
 77700 psi

@Temperature 160 °F
 Dry
627 MPa

@Temperature 24.0 °C
 90900 psi

@Temperature 75.2 °F
 Dry
745 MPa

@Temperature -59.0 °C
 108000 psi

@Temperature -74.2 °F
 Dry
Compressive Modulus 44.8 GPa

@Temperature 71.0 °C
 6500 ksi

@Temperature 160 °F
 Wet
46.9 GPa

@Temperature 93.0 °C
 6800 ksi

@Temperature 199 °F
 Dry
48.3 GPa

@Temperature 71.0 °C
 7010 ksi

@Temperature 160 °F
 Dry
50.3 GPa

@Temperature -59.0 °C
 7300 ksi

@Temperature -74.2 °F
 Dry
51.0 GPa

@Temperature 24.0 °C
 7400 ksi

@Temperature 75.2 °F
 Dry