LATI LASTIROL R-V2 Polystyrene (PS) (UL94 V-2)  (discontinued **)

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI LASTIROL R-V2 Polystyrene (PS) (UL94 V-2)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Lastirol thermoplastics are polystyrene (PS) products. The Lastirols feature excellent dimensional stability, good flowability, and can be molded without any particular problem. Glass fiber reinforced types have high rigidity and excellent dimensional stability.Specific Notes for this Material: UL94V-2 self-extinguishing, with halogens; good flowability; good surface finish; high impact. Disclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
ISO 1183
Water Absorption 0.050 %
0.050 %
at 23°C; ISO 62
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
LATI
Linear Mold Shrinkage, Transverse 0.0030 cm/cm
0.0030 in/in
LATI
Mechanical Properties Metric English Comments
Hardness, Rockwell M 47
47
ASTM D785
Tensile Strength, Ultimate 40.0 MPa
5800 psi
ISO 527
Flexural Modulus 2.75 GPa
399 ksi
ASTM D790
Izod Impact, Notched 0.400 J/cm

@Temperature -40.0 °C
0.749 ft-lb/in

@Temperature -40.0 °F
ASTM D256
0.450 J/cm

@Temperature -20.0 °C
0.843 ft-lb/in

@Temperature -4.00 °F
ASTM D256
0.700 J/cm

@Temperature 23.0 °C
1.31 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 89.0 °C
192 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C
169 °F
ASTM D648
Vicat Softening Point 92.0 °C
198 °F
50°C/h 50N; ISO 306
Flammability, UL94 V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
Oxygen Index 25 %
25 %
ISO 4589
Electrical Properties Metric English Comments
Dielectric Strength 23.0 kV/mm

@Thickness 2.00 mm
584 kV/in

@Thickness 0.0787 in
IEC 243-1
Comparative Tracking Index 525 V
525 V
IEC 112
Processing Properties Metric English Comments
Melt Temperature 170 - 190 °C
338 - 374 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Drying Temperature 60.0 - 70.0 °C
140 - 158 °F
Temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour
>= 3 hour
Drying time can be reduced when using vacuum ovens.
Descriptive Properties Value Comments
Heat Resistance - Ball Test (125°C) N
IEC 335
Heat Resistance - Ball Test (165°C) N
IEC 335
Injection Speed medium - high
Needle Burner Test Y
1.47 mm
Y
3.05 mm