LATI Latamid 66 H2 G/35-V0HF1 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | LATI |
| Trade Name | Latamid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latamid 66 H2 G/35-V0HF1 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0035 - 0.0060 cm/cm | 0.0035 - 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | |
| Elongation at Break | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
|
| Tensile Modulus | 11.5 GPa | 1670 ksi | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | |
| Charpy Impact, Notched | 0.880 J/cm² | 4.19 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 125 °C | 257 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | |
| Vicat Softening Point | 245 °C @Load 5.00 kg |
473 °F @Load 11.0 lb |
|
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
||
| Oxygen Index | 32 % | 32 % | |
| Glow Wire Test | 775 °C @Thickness 1.00 mm |
1430 °F @Thickness 0.0394 in |
GWIT |
| 775 °C @Thickness 2.00 mm |
1430 °F @Thickness 0.0787 in |
GWIT | |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
GWFI/GWT | |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI/GWT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Kolon SPESIN® KP513FLBL Multi Reinforced PBT Resin (discontinued **)
- Humiseal 1B12 Acrylic Conformal Coating
- MetalTek MTEK 304 Cast J92600 Austenitic Stainless Steel
- Shinil Chemical SHINFLAME PBT Flame Retardant Polymer Connector
- Styron DL 242NA Functionalized SB
- Total HDPE 7194 High Density Polyethylene, Specialty Extrusion Resin
- Aaron Industries AAROLENE® ARPE HD 300-2 Black Crate High Density Polyethylene Compounded Resin, Crate Grade
- Multibase C6-180 Dow-Corning Class VI Elastomer
- Saint-Gobain Meldin® 2001 Bearing
- Overview of materials for Polyvinyl Dichloride (PVDC) Coated Polyester Film
Copyright © lookpolymers.com All Rights Reserved