Lanxess Durethan® BKV 30 HTS 901510 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 30 HTS 901510 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 30% glass fibers, very good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 270 °C |
11 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Conditioned; ISO 527-1/-2 |
| 170 MPa | 24700 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 8.0 % | 8.0 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 5.20 GPa | 754 ksi | Conditioned; ISO 527-1/-2 |
| 10.0 GPa | 1450 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU |
| 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Puncture Energy | 7.00 J | 5.16 ft-lb | ISO 6603-2 |
| 12.0 J | 8.85 ft-lb | Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 23 % | 23 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| 4.00e+15 ohm-cm | 4.00e+15 ohm-cm | Conditioned; IEC 60093 | |
| Surface Resistance | 9.00e+11 ohm | 9.00e+11 ohm | IEC 60093 |
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.7 @Frequency 100 Hz |
4.7 @Frequency 100 Hz |
IEC 60250 | |
| 5.1 @Frequency 1.00e+6 Hz |
5.1 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 38 @Frequency 100 Hz |
38 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | Conditioned; IEC 60243-1 |
| 40.0 kV/mm | 1020 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.023 @Frequency 1.00e+6 Hz |
0.023 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.036 @Frequency 100 Hz |
0.036 @Frequency 100 Hz |
IEC 60250 | |
| 0.13 @Frequency 1.00e+6 Hz |
0.13 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.85 @Frequency 100 Hz |
0.85 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 425 V | 425 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MHR,14-110,GF30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- PolyOne OnForce™ LFT LF5200-5001 EM Natural Polyolefin, Unspecified
- Nylacast Oilon Cast Nylon 6, Lubricated (Lubricant Oil Filled)
- Sylvin Technologies 8940-75 Natural PVC Extrusion Compound
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- Alliance BIN-72 Bonded (Composite) Magnetic Material
- Solvay Specialty Polymers Diofan® P530 Polyvinylidene Chloride (PVDC) (discontinued **)
- SABIC Innovative Plastics SABIC STAMAX 60YM240 PP
- LATI Latiohm 66-10 H2 CNT G/35 PA66, 35% Glass Fiber Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved