Mitsui AURUM® JCL3030 Thermoplastic Polyimide Resin, Amorphous, Wear/Friction Grade  (discontinued **)

Category Polymer , Thermoplastic , Polyimide, Thermoplastic
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsui AURUM® JCL3030 Thermoplastic Polyimide Resin, Amorphous, Wear/Friction Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to its semicrystalline state. In addition, it displays low outgassing, superior radiation resistance and excellent chemical resistance properties.Applications: Components for automotive and aircraft enginesTransmissionFarming, off-road and construction equipmentIndustrial machineryElectric motors, pumps and compressorsBusiness machines such as laser pointers and high speed copy machinesElectronic and semiconductor transport mediaAnalytical and medical equipmentConveyors and textile equipmentInformation provided by Mitsui.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ASTM D792
Water Absorption 0.23 %
0.23 %
24 hours; ASTM D570
Moisture Absorption at Equilibrium 0.10 %
0.10 %
24 hours, 23°C, 60% RH
Linear Mold Shrinkage 0.0025 cm/cm
0.0025 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 105
105
ASTM D785
Hardness, Rockwell R 128
128
ASTM D785
Tensile Strength at Break 228.5 MPa
33140 psi
ASTM D638
Tensile Strength, Ultimate 141.2 MPa

@Temperature 150 °C
20480 psi

@Temperature 302 °F
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
4.0 %

@Temperature 150 °C
4.0 %

@Temperature 302 °F
ASTM D638
Flexural Strength 313 MPa
45400 psi
ASTM D790
212 MPa

@Temperature 150 °C
30700 psi

@Temperature 302 °F
ASTM D790
Flexural Modulus 17.2 GPa
2490 ksi
ASTM D790
14.8 GPa

@Temperature 150 °C
2150 ksi

@Temperature 302 °F
ASTM D790
Compressive Strength 102 MPa

@Temperature 150 °C
14800 psi

@Temperature 302 °F
JIS K7208
207 MPa

@Temperature 23.0 °C
30000 psi

@Temperature 73.4 °F
JIS K7208
Compressive Modulus 2.45 GPa
355 ksi
At 150°C; JIS K7208
3.92 GPa
569 ksi
At 23°C; JIS K7208
Shear Strength 60.8 MPa

@Temperature 150 °C
8820 psi

@Temperature 302 °F
JIS K7214
91.2 MPa

@Temperature 23.0 °C
13200 psi

@Temperature 73.4 °F
JIS K7214
Izod Impact, Notched 1.08 J/cm
2.02 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 6.00 µm/m-°C

@Temperature 23.0 °C
3.33 µin/in-°F

@Temperature 73.4 °F
MD; ASTM D696
6.00 µm/m-°C

@Temperature 200 °C
3.33 µin/in-°F

@Temperature 392 °F
MD; ASTM D696
CTE, linear, Transverse to Flow 47.0 µm/m-°C

@Temperature 23.0 °C
26.1 µin/in-°F

@Temperature 73.4 °F
ASTM D696
47.0 µm/m-°C

@Temperature 200 °C
26.1 µin/in-°F

@Temperature 392 °F
ASTM D696
Specific Heat Capacity 0.920 J/g-°C

@Temperature 23.0 °C
0.220 BTU/lb-°F

@Temperature 73.4 °F
By DSC
0.960 J/g-°C

@Temperature 100 °C
0.229 BTU/lb-°F

@Temperature 212 °F
By DSC
1.42 J/g-°C

@Temperature 300 °C
0.339 BTU/lb-°F

@Temperature 572 °F
By DSC
Thermal Conductivity 0.4883 W/m-K
3.383 BTU-in/hr-ft²-°F
Melting Point 388 °C
730 °F
Maximum Service Temperature, Air 248 °C
478 °F
Heat distortion temperature, load unknown; ASTM D648
Glass Transition Temp, Tg 250 °C
482 °F
By DSC
Flammability, UL94 V-0

@Thickness 0.400 mm
V-0

@Thickness 0.0157 in
all color
Electrical Properties Metric English Comments
Surface Resistance 1000 - 10000 ohm
1000 - 10000 ohm
ASTM D257
Processing Properties Metric English Comments
Processing Temperature 390 - 420 °C
734 - 788 °F
Injection molding, extrusion