Mitsui TPX® MX002 Methylpentene Copolymer

Category Polymer , Thermoplastic , Polymethylpentene (PMP)
Manufacturer Mitsui Chemicals America
Trade Name TPX®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsui TPX® MX002 Methylpentene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TPX® is a 4-methylpentene-1 based polyolefin with a unique combination of transparency, heat and chemical resistant qualities. TPX is used in a wide variety of applications, including: medical equipment, laboratory ware, small appliances, ovenware, baking cartons, release paper, wire and cable coating, and a number of industrial uses. TPX is manufactured and marketed solely by Mitsui Chemicals, Inc.Applications: Injection Molded Items: Blood test cellsMedical instrumentsLaboratory wareCoffee maker partsCosmetic containersExtrusion Molded Items: Sight glass (pipes, sheets)Baking cartons (food containers)Release paperWire and cable coatingFilmsMolding Method: InjectionExtrusionBlowInformation provided by Mitsui.
Physical Properties Metric English Comments
Density 0.835 g/cc
0.0302 lb/in³
ASTM D1505
Water Absorption 0.010 %
0.010 %
24 hours; ASTM D570
Linear Mold Shrinkage 0.016 cm/cm
0.016 in/in
MPC method, MD
Linear Mold Shrinkage, Transverse 0.016 cm/cm
0.016 in/in
MPC method
Melt Flow 22 g/10 min

@Load 5.00 kg,
Temperature 260 °C
22 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 35
35
ASTM D785
Tensile Strength at Break 15.7 MPa
2280 psi
5mm/min; ASTM D638
Tensile Strength, Yield 14.7 MPa
2130 psi
5mm/min; ASTM D638
Elongation at Break 120 %
120 %
MPC method, 5mm/min
Modulus of Elasticity 0.490 GPa
71.1 ksi
Tangent; ASTM D790
Flexural Strength 19.6 MPa
2840 psi
2mm/min; ASTM D790
Flexural Stiffness 386 MPa
56000 psi
Olsen Stiffness; ASTM D747
Izod Impact, Unnotched (ISO) 48.3 kJ/m²

@Thickness 2.00 mm,
Temperature 20.0 °C
23.0 ft-lb/in²

@Thickness 0.0787 in,
Temperature 68.0 °F
ASTM D256
Charpy Impact, Notched 0.420 J/cm²

@Thickness 2.00 mm,
Temperature 20.0 °C
2.00 ft-lb/in²

@Thickness 0.0787 in,
Temperature 68.0 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 117 µm/m-°C

@Temperature 20.0 °C
65.0 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Specific Heat Capacity 1.97 J/g-°C
0.471 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.167 W/m-K
1.16 BTU-in/hr-ft²-°F
BS 874A
Melting Point 235 °C
455 °F
MPC Method
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C
176 °F
ASTM D648
Vicat Softening Point 145 °C
293 °F
ASTM D1525
Optical Properties Metric English Comments
Refractive Index 1.463
1.463
n20 D; ASTM D542
Haze 2.0 %
2.0 %
ASTM D1746
Transmission, Visible 80 %
80 %
Mfr. indicates clear but does not quantify
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 2.12

@Frequency 100 - 1.00e+6 Hz
2.12

@Frequency 100 - 1.00e+6 Hz
ASTM D150
Dielectric Strength 63.0 kV/mm
1600 kV/in
ASTM D149
Descriptive Properties Value Comments
Appearance Colorless transparent
Rate of Burning 2.54 cm/min
ASTM D635