Omnia Plastica Akulon® PA6 G.Oil - Omniamid Oil - at 50% RH

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Cast
Manufacturer Omnia Plastica s.p.a.
Trade Name Akulon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Omnia Plastica Akulon® PA6 G.Oil - Omniamid Oil - at 50% RH.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cast Nylon 6 with the addition of 6% of special lubricating oil which remains in solution in the material. The unique method of production results in a micro distribution of oil particles with a homogeneous dispersion. This produces a notable improvement in the self-lubrication property as well as the shock resistance. Machining is also much easier.Features:Self-lubricating: the friction coefficient is the lowest of all the cast nylons.Wear resistance: better than PA6 natural.Tensile stress and compressive strength is like Omniamid G whilst shock resistance is higher, the E-modulus is lower.Machining: excellent on machine tools.Colour: orange and black.Weak Point:It is hygroscopic, even if to a lower extent than natural PA6 G. Because of the molecular structure, the large-sized cast pieces have better quality than those of small dimensions.Application:Mechanical: thanks to its excellent self-lubricating property, high shock resistance and compressive strength, together with the possibility to produce large-sized parts, it is widely used to produce bearings and bushings of large diameters as well as pulleys, wheels and anti-wear guides. Because of its excellent abrasion resistance it is used for gear wheels, guide bearings, bearings, sliding bearings, etc. in the building of parts for construction machines, excavators and earthmovers. In the shipbuilding industry its better weather resistance makes it suitable for rollers, haulage, sliding guides, bearings. In cable-car systems its usage includes pulleys, wheels and sliding blocks.Food contact: it cannot be used in contact with foodElectrical: usage in the electrical field is to be avoided as the electrical properties change with the change in moisture content.Chemical: it is resistant to alkali, inorganic compounds and solvents.Information provided by Omnia Plastica s.p.a. for semifinished products such as sheet, rod, and tube.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO.1183 DIN.53479
Moisture Absorption at Equilibrium 1.5 %
1.5 %
50% relative humidity (beginning dry)
Water Absorption at Saturation 4.8 %
4.8 %
23°C (beginning dry)
Mechanical Properties Metric English Comments
Ball Indentation Hardness 80.0 MPa
11600 psi
ISO2039.1 DIN.53456
Tensile Strength at Break 50.0 MPa
7250 psi
ISO.527 DIN.53455
Elongation at Break 120 %
120 %
ISO.527 DIN.53455
Tensile Modulus 1.70 GPa
247 ksi
ISO.527 DIN.53455
Compressive Strength 6.00 MPa
870 psi
1% strain over 1000 hours; ISO.899 DIN.53444
Charpy Impact Unnotched NB
NB
7.5 J; ISO.R179 DIN.53453
Charpy Impact, Notched 2.50 J/cm²
11.9 ft-lb/in²
ISO179/3C DIN.53453
Coefficient of Friction, Dynamic 0.34
0.34
on dry ground steel; load =0.05MPa; speed =0.6 m/s (dry sample)
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
dry sample
Thermal Conductivity 0.280 W/m-K
1.94 BTU-in/hr-ft²-°F
DIN.52612 (dry sample)
Melting Point 220 °C
428 °F
Maximum Service Temperature, Air 100 °C
212 °F
Maximum operating temperature continuously for 5000 hours based on a tensile stress of 50% at 23° C. (dry sample)
160 °C
320 °F
short period, no load (dry sample)
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
ISO.75 DIN.53461 (dry sample)
Minimum Service Temperature, Air -30.0 °C
-22.0 °F
impact conditions and heavy loads not considered (dry sample)
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Dielectric Constant 7.0

@Frequency 1e+6 Hz
7.0

@Frequency 1e+6 Hz
ISO.250 DIN.53483