Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether + Styrene-Butadiene Blend". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.06 - 1.10 g/cc
0.0383 - 0.0397 lb/in³
Average value: 1.07 g/cc Grade Count:9
Water Absorption 0.300 - 0.400 %
0.300 - 0.400 %
Average value: 0.356 % Grade Count:9
Moisture Absorption at Equilibrium 0.100 - 0.150 %
0.100 - 0.150 %
Average value: 0.128 % Grade Count:9
Linear Mold Shrinkage 0.00600 cm/cm
0.00600 in/in
Average value: 0.00600 cm/cm Grade Count:9
Melt Flow 8.00 - 130 g/10 min
8.00 - 130 g/10 min
Average value: 64.2 g/10 min Grade Count:9
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 - 80.0 MPa
7250 - 11600 psi
Average value: 62.7 MPa Grade Count:9
Elongation at Break 20.0 - 50.0 %
20.0 - 50.0 %
Average value: 35.0 % Grade Count:9
Elongation at Yield 4.00 - 6.00 %
4.00 - 6.00 %
Average value: 5.00 % Grade Count:9
Modulus of Elasticity 2.20 - 2.80 GPa
319 - 406 ksi
Average value: 2.54 GPa Grade Count:9
Charpy Impact Unnotched 5.00 J/cm² - NB
23.8 ft-lb/in² - NB
Average value: 5.00 J/cm² Grade Count:9
1.00 J/cm² - NB

@Temperature -30.0 - -30.0 °C
4.76 ft-lb/in² - NB

@Temperature -22.0 - -22.0 °F
Average value: 2.19 J/cm² Grade Count:9
Charpy Impact, Notched 1.60 - 3.20 J/cm²
7.61 - 15.2 ft-lb/in²
Average value: 2.22 J/cm² Grade Count:9
1.60 - 3.20 J/cm²

@Temperature -30.0 - -30.0 °C
7.61 - 15.2 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 2.22 J/cm² Grade Count:9
Tensile Creep Modulus, 1000 hours 1850 - 1950 MPa
268000 - 283000 psi
Average value: 1900 MPa Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 65.0 µm/m-°C
36.1 µin/in-°F
Average value: 65.0 µm/m-°C Grade Count:9
Deflection Temperature at 0.46 MPa (66 psi) 107 - 157 °C
225 - 315 °F
Average value: 126 °C Grade Count:9
Deflection Temperature at 1.8 MPa (264 psi) 100 - 140 °C
212 - 284 °F
Average value: 114 °C Grade Count:9
Vicat Softening Point 108 - 160 °C
226 - 320 °F
Average value: 128 °C Grade Count:9
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:9
Oxygen Index 22.0 - 37.0 %
22.0 - 37.0 %
Average value: 27.0 % Grade Count:4
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Average value: 1.00e+15 ohm-cm Grade Count:9
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Average value: 1.00e+14 ohm Grade Count:9
Dielectric Constant 2.50 - 2.90
2.50 - 2.90
Average value: 2.69 Grade Count:9
Dielectric Strength 90.0 - 95.0 kV/mm
2290 - 2410 kV/in
Average value: 91.7 kV/mm Grade Count:9
Dissipation Factor 0.000500 - 0.00600
0.000500 - 0.00600
Average value: 0.00272 Grade Count:9
Comparative Tracking Index 250 - 300 V
250 - 300 V
Average value: 283 V Grade Count:9