SABIC Innovative Plastics Cycoloy® C1200 PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C1200 PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CYCOLOY C1200 is a PC+ABS blend developed to serve extremely demanding applications in a variety of markets while maintaining good processing properties. The combination of superior heat resistance and excellent sub zero temperature ductility makes CYCOLOY C1200 the ideal candidate for high load and impact zone applications in automotive components,This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.60 %

@Temperature 23.0 °C
0.60 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on tensile bar; SABIC Method
Melt Flow 12 g/10 min

@Load 5.00 kg,
Temperature 260 °C
12 g/10 min

@Load 11.0 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ISO 2039-2
Hardness, H358/30 99.0 MPa
14400 psi
ISO 2039-1
Tensile Strength at Break 40.0 MPa
5800 psi
5 mm/min; ISO 527
50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield 50.0 MPa
7250 psi
5 mm/min; ISO 527
55.0 MPa
7980 psi
50 mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50 mm/min; ISO 527
100 %
100 %
5 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527
Flexural Yield Strength 85.0 MPa
12300 psi
2 mm/min; ISO 178
Flexural Modulus 2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 30.0 kJ/m²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
50.0 kJ/m²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 3.00 J/cm²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles 63

@Load 1.00 kg
63

@Load 2.20 lb
CS-17; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test <= 125 °C
<= 257 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 130 °C
266 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 132 °C
270 °F
Rate B/50; ISO 306
134 °C
273 °F
Rate B/120; ISO 306
UL RTI, Electrical 105 °C
221 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 105 °C
221 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.20 mm
HB

@Thickness 0.0472 in
UL 94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
2nd value; UL 94
Glow Wire Test 650 °C

@Thickness 1.00 mm
1200 °F

@Thickness 0.0394 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
2.8

@Frequency 50.0 - 60.0 Hz
2.8

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
635 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
35.0 kV/mm

@Thickness 0.800 mm
889 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.0020

@Frequency 50.0 - 60.0 Hz
0.0020

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 250 - 400 V
250 - 400 V
PLC code 2; UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES