SABIC Innovative Plastics LNP Stat-kon RX89129 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon RX89129 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Kon RX89129 is a compound based on Nylon 6,6. Fillers are proprietary.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.94 % | 0.94 % | 23°C / 50% RH; ISO 62 |
| 0.62 % @Time 86400 sec |
0.62 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 67.0 MPa | 9720 psi | 5 mm/min; ISO 527 |
| 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 68.0 MPa | 9860 psi | 5 mm/min; ISO 527 |
| 69.0 MPa | 10000 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D 638 |
| 4.1 % | 4.1 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D 638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.31 GPa | 480 ksi | 1 mm/min; ISO 527 |
| 3.45 GPa | 500 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.59 GPa | 376 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 3.10 GPa | 450 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm @Temperature 23.0 °C |
0.787 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 7.15 J/cm @Temperature 23.0 °C |
13.4 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 44.0 kJ/m² @Temperature 23.0 °C |
20.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
45.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
48.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 224 °C @Thickness 3.20 mm |
435 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 91.0 °C @Thickness 3.20 mm |
196 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 3.0 ohm | 1.0 - 3.0 ohm | ASTM D 257 |