SABIC Innovative Plastics LNP Thermotuf U1000AIS PPA (Asia Pacific)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Thermotuf
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermotuf U1000AIS PPA (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermotuf* U1000AIS is a compound based on Polyphthalamide resin. Added features of this material include: High Impact, Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
1.12 g/cc
0.0405 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.014 cm/cm

@Time 86400 sec
0.014 in/in

@Time 24.0 hour
ASTM D 955
0.014 cm/cm

@Time 86400 sec
0.014 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.017 cm/cm

@Time 86400 sec
0.017 in/in

@Time 24.0 hour
ASTM D 955
0.017 cm/cm

@Time 86400 sec
0.017 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 56.0 MPa
8120 psi
ISO 527
58.0 MPa
8410 psi
ASTM D 638
Tensile Strength, Yield 56.0 MPa
8120 psi
ISO 527
59.0 MPa
8560 psi
ASTM D 638
Elongation at Break 12.6 %
12.6 %
ISO 527
17 %
17 %
ASTM D 638
Elongation at Yield 5.0 %
5.0 %
ASTM D 638
7.3 %
7.3 %
ISO 527
Tensile Modulus 2.45 GPa
355 ksi
1 mm/min; ISO 527
2.75 GPa
399 ksi
50 mm/min; ASTM D 638
Flexural Strength 79.0 MPa
11500 psi
ISO 178
Flexural Modulus 2.00 GPa
290 ksi
ISO 178
2.06 GPa
299 ksi
ASTM D 790
Izod Impact, Notched 5.87 J/cm

@Temperature 23.0 °C
11.0 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 19.22 J/cm

@Temperature 23.0 °C
36.01 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 44.0 kJ/m²

@Temperature 23.0 °C
20.9 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 172 kJ/m²

@Temperature 23.0 °C
81.8 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 52.0 J
38.4 ft-lb
Multiaxial Impact; ISO 6603
6.00 J

@Temperature 23.0 °C
4.43 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 79.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
79.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
81.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
45.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 153 °C
307 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
157 °C

@Thickness 3.20 mm
315 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 108 °C
226 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
108 °C

@Thickness 3.20 mm
226 °F

@Thickness 0.126 in
unannealed; ASTM D 648