SABIC Innovative Plastics NORYL GTX GTX987 PPE+PA66 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL GTX GTX987 PPE+PA66 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Conductive GTX, CTE 7
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Density 1.25 g/cc
0.0452 lb/in³
ISO 1183
Moisture Absorption 0.900 %
0.900 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 3.0 %
3.0 %
ISO 62
Linear Mold Shrinkage, Flow 0.010 - 0.014 cm/cm

@Thickness 3.20 mm
0.010 - 0.014 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.5 g/10 min

@Load 5.00 kg,
Temperature 280 °C
8.5 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
7.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
62.0 MPa
8990 psi
50 mm/min; ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
62.0 MPa
8990 psi
50 mm/min; ISO 527
Elongation at Break 15 %
15 %
Type I, 50 mm/min; ASTM D638
20 %
20 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 3.00 GPa
435 ksi
1 mm/min; ISO 527
3.25 GPa
471 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.70 GPa
392 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.80 GPa
406 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.900 J/cm
1.69 ft-lb/in
ASTM D256
0.700 J/cm

@Temperature -30.0 °C
1.31 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 10.0 J

@Temperature 23.0 °C
7.38 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.0 µm/m-°C

@Temperature -40.0 - 60.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 140 °F
ASTM E 831
70.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 60.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 140 °F
ASTM E 831
75.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
41.7 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
185 °C

@Thickness 3.20 mm
365 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 192 °C
378 °F
Rate B/50; ASTM D1525
198 °C
388 °F
Rate B/50; ISO 306
200 °C
392 °F
Rate B/120; ISO 306