Solvay Specialty Polymers Ixef® GS-1022 Polyarylamide (PARA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® GS-1022 Polyarylamide (PARA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef GS-1022 is a 50% glass-fiber reinforced grade of polyarylamide (PARA) available in several colors. Parts molded from these colored resins can withstand high-energy gamma radiation without significant change in appearance and physical properties. Ixef GS-1022 resins demonstrate no evidence of cytotoxicity, sensitization, intracutaneous reactivity or acute systemic toxicity, based on biocompatibility testing as defined by ISO 10993-1. This resin offers superior strength and stiffness combined with outstanding surface gloss and exceptional flow and is well suited for medical applications, such as single use surgical instruments and structural device housings, and applications in food service equipment. Colors available: - Brown: GS-1022 BN01 - Blue: GS-1022 BU01 - Green: GS-1022 GN01 - Grey: GS-1022 GY01 - Grey: GS-1022 GY02 - Grey: GS-1022 GY51 - White: GS-1022 WH01 - Black: 1022/9006Additional Information: Property values for individual batches will vary within specification limits. Values shown are typical of Ixef GS-1022/WH01 resin; other colorants may alter values. There will be a shift in color when comparing pre-gamma sterilization and postgamma sterilization colors. It is also expected that the colors will revert to some degree, back toward the as-molded color. Lighter colors may display the greatest variation.Injection Notes: Hot runners: 250° to 260°C (482° to 500°F)Data is presented for dry polymer.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
ISO 1183
Filler Content 50 %
50 %
Glass Fiber Reinforcement
Water Absorption 0.16 %

@Temperature 23.0 °C,
Time 86400 sec
0.16 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
65% RH; Internal Method
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 265 MPa
38400 psi
ISO 527-2
Elongation at Break 1.8 %
1.8 %
ISO 527-2
Tensile Modulus 22.0 GPa
3190 ksi
ISO 527-2
Flexural Strength 380 MPa
55100 psi
ISO 178
Flexural Modulus 22.0 GPa
3190 ksi
ISO 178
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear 15.0 µm/m-°C
8.33 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Nozzle Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 280 °C
536 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C
248 °F
Dry Time 0.500 - 1.50 hour
0.500 - 1.50 hour
Descriptive Properties Value Comments
Additive Gamma Stabilizer
Agency Ratings ISO 10993
ISO 10993-Part 1
Appearance Black
Colors Available
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Biocompatible
E-beam Sterilizable
Ethylene Oxide Sterilizable
Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
Good Sterilizability
High Flow
High Strength
Low Moisture Absorption
Outstanding Surface Finish
Radiation (Gamma) Resistant
Radiation Sterilizable
Radiotranslucent
Ultra High Stiffness
Forms Pellets
Generic PARA
Injection Rate Fast
Processing Method Injection Molding
Uses Dental Applications
Hospital Goods
Medical Appliances
Medical/Healthcare Applications
Surgical Instruments