Sumitomo Bakelite North America 51-01 CAFR-P Mineral Filled Diallyl Phthalate

Category	Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP), Cast, Mineral Filler , Filled/Reinforced Thermoset
Manufacturer	Sumitomo Bakelite North America
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sumitomo Bakelite North America 51-01 CAFR-P Mineral Filled Diallyl Phthalate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Information provided by Sumitomo Bak North America, Inc.

Physical Properties	Metric	English	Comments
Density	1.75 g/cc	0.0632 lb/inÂ³	ASTM D792
Apparent Bulk Density	0.760 g/cc	0.0275 lb/inÂ³
Water Absorption	0.55 %	0.55 %	48 hours, 50Â°C. ASTM D570
Linear Mold Shrinkage	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	Compression Molding. ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	55.0 MPa	7980 psi	ASTM D638
Flexural Yield Strength	90.0 MPa	13100 psi	ASTM D790
Flexural Modulus	8.30 GPa	1200 ksi	ASTM D790
Compressive Yield Strength	145 MPa	21000 psi	ASTM D695
Izod Impact, Notched	0.210 J/cm	0.393 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	34.0 Âµm/m-Â°C @Temperature 20.0 Â°C	18.9 Âµin/in-Â°F @Temperature 68.0 Â°F	ASTM D696
Maximum Service Temperature, Air	130 Â°C	266 Â°F	UL temperature Index, UL 746B
Deflection Temperature at 1.8 MPa (264 psi)	163 Â°C	325 Â°F	ASTM D648A
UL RTI, Electrical	130 Â°C	266 Â°F	UL temperature Index, UL 746B
UL RTI, Mechanical with Impact	130 Â°C	266 Â°F	UL temperature Index, UL 746B
UL RTI, Mechanical without Impact	130 Â°C	266 Â°F	UL temperature Index, UL 746B
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
Oxygen Index	30 %	30 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Dielectric Constant	4.3 @Frequency 1e+6 Hz	4.3 @Frequency 1e+6 Hz	Wet
	4.5 @Frequency 1000 Hz	4.5 @Frequency 1000 Hz	Wet
Dielectric Strength	15.0 kV/mm	381 kV/in	Wet, step-by-step. ASTM D149
	16.0 kV/mm	406 kV/in	Wet, short term. ASTM D149
Dissipation Factor	0.020 @Frequency 1000 Hz	0.020 @Frequency 1000 Hz	Wet; ASTM D150
	0.025 @Frequency 1e+6 Hz	0.025 @Frequency 1e+6 Hz	Wet; ASTM D150
Arc Resistance	135 sec	135 sec	ASTM D495
Comparative Tracking Index	>= 600 V	>= 600 V	UL746A, ASTM D3638
Hot Wire Ignition, HWI	30 - 59 sec @Thickness 1.57 mm	30 - 59 sec @Thickness 0.0618 in	UL PLC 2 (30-59 sec)
High Amp Arc Ignition, HAI	15 - 29 arcs @Thickness 1.57 mm	15 - 29 arcs @Thickness 0.0618 in	UL PLC 3 (15-29 arcs)
High Voltage Arc-Tracking Rate, HVTR	0.000 - 10.0 mm/min @Thickness 1.57 mm	0.000 - 0.394 in/min @Thickness 0.0618 in	UL PLC 0 (0-10 mm/min)

Processing Properties	Metric	English	Comments
Processing Temperature	160 - 180 Â°C	320 - 356 Â°F	Mold temperature