Tisan TISAKRIL® UNR ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Tisan Engineering Plastics
Trade Name TISAKRIL®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tisan TISAKRIL® UNR ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TISAKRIL has a wide area of application in automotive, electronics, computer, construction, and furniture industries. General Specifications include: High surface luminosityEasy processabilityDimensional stabilityInsulationLow weightHigh toughnessLow moisture absorptionHigh chemical resistance Glass fiber reinforced TISAKRIL increases mechanical resistance, surface hardness, melting point and specific gravity, while simultaneously reducing mold shrinkage. Calcite, talc, glass ball and other fillers may be used for reinforcement of TISAKRIL apart from glass fiber. It has excellent chemical resistance to weak acids, weak alkalis, and strong alkalis. It has good resistance against strong acids. It has weak chemical resistance against organic solvents, alcohols, hydrocarbons, and engine fuels.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
ISO 527-2
Tensile Strength, Yield 45.0 MPa
6530 psi
ISO 527-2
Elongation at Break 4.0 %
4.0 %
ISO 527-2
Elongation at Yield 4.0 %
4.0 %
ISO 527-2
Modulus of Elasticity 2.40 GPa
348 ksi
ISO 527-2
Izod Impact, Notched (ISO) 15.0 - 20.0 kJ/m²
7.14 - 9.52 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 177 °C
351 °F
Vicat Softening Point 102 °C
216 °F
ISO 306
Heat Distortion Temperature 97.0 °C
207 °F
ISO 75-2
Flammability, UL94 HB
HB
Glow Wire Test 650 °C
1200 °F
60695-2-10
Electrical Properties Metric English Comments
Comparative Tracking Index 500 V
500 V
TS EN 60112
Processing Properties Metric English Comments
Feed Temperature 60.0 °C
140 °F
Rear Barrel Temperature 190 - 210 °C
374 - 410 °F
Aft-1. Region Temperature
Middle Barrel Temperature 190 - 210 °C
374 - 410 °F
Mid-2. Region Temperature
Front Barrel Temperature 190 - 210 °C
374 - 410 °F
Pre-3. Region Temperature
Nozzle Temperature 200 °C
392 °F
Melt Temperature 160 - 180 °C
320 - 356 °F
Drying Temperature 80.0 °C
176 °F
Predrying Temperature
Dry Time 2 - 3 hour
2 - 3 hour
Predrying Time
Moisture Content 0.30 %
0.30 %
ISO 62
Descriptive Properties Value Comments
Block Temperature 45°C