Total Finathene® 3344N Natural HDPE pipe grade  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , MDPE , Medium Density Polyethylene (MDPE), Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Finathene® 3344N Natural HDPE pipe grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: industrial and mining gas distribution, potable water, sewer and sewer relining, gas and oil gathering, fiber optic innerduct, general pipe reliningInformation provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Density 0.947 g/cc
0.0342 lb/in³
ASTM D 792
Environmental Stress Crack Resistance >= 1000 hour
>= 1000 hour
No failures, compressed ring, 25% Igepal; ASTM F 1248
>= 5000 hour
>= 5000 hour
No failures; ASTM D 1693 cond. C
Melt Flow 0.090 g/10 min

@Load 2.16 kg
0.090 g/10 min

@Load 4.76 lb
ASTM D 1238
0.34 g/10 min

@Load 5.00 kg
0.34 g/10 min

@Load 11.0 lb
ASTM D 1238
High Load Melt Index 9.0 g/10 min

@Load 21.6 kg
9.0 g/10 min

@Load 47.6 lb
ASTM D 1238
Mechanical Properties Metric English Comments
PENT >= 500 hour
>= 500 hour
ASTM F 1473
Hardness, Rockwell L 49
49
ASTM D 785
Hardness, Shore D 63
63
ASTM D 2240
Tensile Strength, Yield >= 22.8 MPa
>= 3300 psi
ASTM D 638 type IV
Elongation at Break >= 800 %
>= 800 %
ASTM D 638 type IV
Flexural Modulus 0.862 GPa
125 ksi
ASTM D 790
Secant Modulus 0.793 GPa
115 ksi
2% Strain; ASTM D 638 type IV
Izod Impact, Notched 4.27 J/cm

@Thickness 3.17 mm
8.00 ft-lb/in

@Thickness 0.125 in
ASTM D256 A
Hydrostatic Design Basis 11.0 MPa

@Temperature 23.0 °C
1600 psi

@Temperature 73.4 °F
ASTM D 2837
Thermal Properties Metric English Comments
CTE, linear 180 µm/m-°C

@Temperature 20.0 °C
100 µin/in-°F

@Temperature 68.0 °F
ASTM D 696
Melting Point 131 °C
268 °F
ASTM D3417
Deflection Temperature at 0.46 MPa (66 psi) 77.8 °C
172 °F
ASTM D 648
Vicat Softening Point 124 °C
255 °F
ASTM D 1525
Brittleness Temperature -118 °C
-180 °F
ASTM D 746