Total HDPE HL 535 High Density Polyethylene, Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Total Atofina
Trade Name HDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total HDPE HL 535 High Density Polyethylene, Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyethylene: Medium molecular weight, high density film resinCharacteristics:High stiffnessGood heat resistanceExcellent bubble stabilityGood compatibility with LDPE and LLDPEApplications:Release linersStand-up bagsCoextruded filmsInformation provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.955 g/cc
0.955 g/cc
ASTM D792
Water Vapor Transmission 10.9 g/m²/day

@Temperature 37.8 °C
0.700 g/100 in²/day

@Temperature 100 °F
ASTM F1249
Melt Flow 0.35 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.35 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
30 g/10 min

@Load 21.6 kg,
Temperature 190 °C
30 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 27.6 MPa
4000 psi
ASTM D882, A 20 in/min
Film Tensile Strength at Yield, TD 29.6 MPa
4300 psi
ASTM D882, A 20 in/min
Film Elongation at Break, MD 500 %
500 %
ASTM D882, A 20 in/min
Film Elongation at Break, TD 25 %
25 %
ASTM D882, A 20 in/min
Elmendorf Tear Strength MD 8.0 g
8.0 g
ASTM D1922
Elmendorf Tear Strength TD 1100 g
1100 g
ASTM D1922
Dart Drop Test >= 50.0 g
>= 0.110 lb
ASTM D1709, A
Film Tensile Strength at Break, MD 43.4 MPa
6300 psi
ASTM D882, A 20 in/min
Film Tensile Strength at Break, TD 29.6 MPa
4300 psi
ASTM D882, A 20 in/min
1% Secant Modulus, MD 917 MPa
133000 psi
1 in/min; ASTM D882
1% Secant Modulus, TD 1280 MPa
186000 psi
1 in/min; ASTM D882
Thermal Properties Metric English Comments
Melting Point 132 °C
270 °F
ASTM D3417
Processing Properties Metric English Comments
Melt Temperature 193 - 216 °C
380 - 420 °F
Extrusion