Toyobo GLAMIDE® T-663G30 Nylon-66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® T-663G30 Nylon-66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-663G30 is a GF reinforced Nylon-66. It contains 30% GF.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.60 % | 0.60 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm @Thickness 1.00 mm |
0.0020 - 0.0050 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0060 - 0.0090 cm/cm @Thickness 3.00 mm |
0.0060 - 0.0090 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 100 MPa @Temperature 80.0 °C |
14500 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.75%); ASTM-D638 |
| 120 MPa @Temperature 80.0 °C |
17400 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 145 MPa @Temperature 23.0 °C |
21000 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.75%); ASTM-D638 | |
| 195 MPa @Temperature 23.0 °C |
28300 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 215 MPa @Temperature -40.0 °C |
31200 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.75%); ASTM-D638 | |
| 235 MPa @Temperature -40.0 °C |
34100 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 3.2 % | 3.2 % | Absolute Drying; ASTM-D638 |
| 3.9 % | 3.9 % | Practical Use (Water Absorption 1.75%); ASTM-D638 | |
| Flexural Strength | 130 MPa @Temperature 80.0 °C |
18900 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.75%); ASTM-D790 |
| 185 MPa @Temperature 80.0 °C |
26800 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 210 MPa @Temperature 23.0 °C |
30500 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.75%); ASTM-D790 | |
| 280 MPa @Temperature 23.0 °C |
40600 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 300 MPa @Temperature -40.0 °C |
43500 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.75%); ASTM-D790 | |
| 315 MPa @Temperature -40.0 °C |
45700 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 4.00 GPa @Temperature 80.0 °C |
580 ksi @Temperature 176 °F |
Practical Use (Water Absorption 1.75%); ASTM-D790 |
| 5.40 GPa @Temperature 80.0 °C |
783 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 5.80 GPa @Temperature 23.0 °C |
841 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.75%); ASTM-D790 | |
| 8.70 GPa @Temperature 23.0 °C |
1260 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 9.80 GPa @Temperature -40.0 °C |
1420 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.75%); ASTM-D790 | |
| 10.8 GPa @Temperature -40.0 °C |
1570 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 0.700 J/cm @Temperature -40.0 °C |
1.31 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.800 J/cm @Temperature -40.0 °C |
1.50 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 1.75%); ASTM-D256 | |
| 1.10 J/cm @Temperature 23.0 °C |
2.06 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 1.40 J/cm @Temperature 23.0 °C |
2.62 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 1.75%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 - 1.00e+10 ohm-cm | 1.00e+9 - 1.00e+10 ohm-cm | Practical Use (Water Absorption 1.75%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Constant | 4.1 @Frequency 1000 Hz |
4.1 @Frequency 1000 Hz |
Absolute Drying; ASTM-D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 1.75%); ASTM-D149 |
| 26.0 kV/mm @Thickness 2.00 mm |
660 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 92 sec | 92 sec | Practical Use (Water Absorption 1.75%); ASTM-D495 |
| 100 sec | 100 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | 575 V | 575 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Injection Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi |