BASF Ultramid® 8333G HI HS BK 106 33% Glass Filled PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8333G HI HS BK 106 33% Glass Filled PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description Ultramid 8333G HI HS BK-102 is a 33% glass reinforced, impact modified PA6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics.Applications: front wheel chair wheels, bicycle wheels, power tool housings, chain saw housings, clips and fasteners, hose clamps and window hardware.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.36 g/cc	0.0491 lb/in³	ASTM D792
Moisture Absorption at Equilibrium	0.90 %	0.90 %	24 hour; ASTM D570
	1.5 %	1.5 %	50% RH; ASTM D570
	5.5 %	5.5 %	Saturation; ASTM D570
Linear Mold Shrinkage	0.00762 cm/cm	0.00762 in/in	1/8" bar

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	121	121
Tensile Strength at Break	145 MPa	21000 psi	ASTM D638
Elongation at Break	2.5 %	2.5 %	ASTM D638
Flexural Strength	232 MPa	33600 psi	ISO 790
Flexural Modulus	7.99 GPa	1160 ksi	ISO 178
Izod Impact, Notched (ISO)	182 kJ/m²	86.6 ft-lb/in²	ISO 3146

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi)	208 °C	406 °F	ASTM D648

Processing Properties	Metric	English	Comments
Zone 1	245 - 275 °C	473 - 527 °F	Rear Zone
Zone 2	260 - 285 °C	500 - 545 °F	Center Zone
Zone 3	270 - 295 °C	518 - 563 °F	Front Zone
Zone 4	270 - 295 °C	518 - 563 °F	Nozzle
Melt Temperature	270 - 295 °C	518 - 563 °F
Mold Temperature	80.0 - 95.0 °C	176 - 203 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	<= 0.080 %	<= 0.080 %

Descriptive Properties	Value	Comments
Color	BK 106
Commercial Status	North America