LG Chemical LUMID HI1102A(W) PA6, High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI1102A(W) PA6, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6, High ImpactApplication: H/Lamp Screw MountingCAS No. 25038-54-4 and 9010-79-1Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Water Absorption | 1.4 % | 1.4 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.016 cm/cm @Thickness 3.20 mm |
0.012 - 0.016 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 66.7 MPa @Thickness 3.20 mm |
9670 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 80 % @Thickness 3.20 mm |
80 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 83.4 MPa @Thickness 3.20 mm |
12100 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa @Thickness 3.20 mm |
313 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 1.67 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
3.12 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C @Thickness 6.40 mm |
302 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C @Thickness 6.40 mm |
122 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 19.0 kV/mm @Thickness 1.00 mm |
483 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 195 sec | 195 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Front Barrel Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Nozzle Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Radici Heraflex® A 90-21-90 TPS-SEBS Thermoplastic Elastomer
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Hi-Sil 233 Filler
- Magyar Aluminum ALO-EL-4F Alumina
- Solvay RHODACAL® SSA/A Surfactant
- SABIC Innovative Plastics LNP THERMOCOMP 9X94104 PEI (Europe-Africa-Middle East)
- Supreme Petrochem SH 2114 High Impact Polystyrene
- Tisan TISOPLEN® Flame Retardant (V0). Heat Stabilized, Copolymer Polypropylene
- Zircar Refractory Composites ASPA-880 Alumina-Silica Fiber Paper
- ConocoPhillips ANDEROL® FGH 100 Synthetic Food Grade Hydraulic Fluid, ISO 100
- Overview of materials for Ethylene-Methyl Acrylate Copolymer, Film Grade
Copyright © lookpolymers.com All Rights Reserved