POLYMER SEARCH

LG Chemical LUPOL GP1000FC Flame Retardant PP

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer	LG Chemical
Trade Name	LUPOL
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	LG Chemical LUPOL GP1000FC Flame Retardant PP.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description: Injection Molding, FR PP, General Purpose, Flame RetardantApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 1309-64-4Information provided by LG Chemical

Physical Properties	Metric	English	Comments
Specific Gravity	1.00 g/cc	1.00 g/cc	ASTM D792
Maximum Moisture Content	0.010	0.010	Injection Molding
Linear Mold Shrinkage, Flow	0.016 - 0.018 cm/cm <br>@Thickness 3.20 mm	0.016 - 0.018 in/in <br>@Thickness 0.126 in	ASTM D955
Melt Flow	14 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 Â°C	14 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	32.4 MPa <br>@Thickness 3.20 mm	4690 psi <br>@Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	70 % <br>@Thickness 3.20 mm	70 % <br>@Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	38.2 MPa <br>@Thickness 6.40 mm	5550 psi <br>@Thickness 0.252 in	10mm/min; ASTM D790
Flexural Modulus	1.77 GPa <br>@Thickness 6.40 mm	256 ksi <br>@Thickness 0.252 in	10mm/min; ASTM D790
Izod Impact, Notched	0.490 J/cm <br>@Thickness 6.40 mm,<br> Temperature 23.0 Â°C	0.918 ft-lb/in <br>@Thickness 0.252 in,<br> Temperature 73.4 Â°F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	120 Â°C <br>@Thickness 3.20 mm	248 Â°F <br>@Thickness 0.126 in	Unannealed; ASTM D648
UL RTI, Electrical	120 Â°C <br>@Thickness >=0.750 mm	248 Â°F <br>@Thickness >=0.0295 in
	120 Â°C <br>@Thickness >=1.50 mm	248 Â°F <br>@Thickness >=0.0591 in
	120 Â°C <br>@Thickness >=3.00 mm	248 Â°F <br>@Thickness >=0.118 in
UL RTI, Mechanical with Impact	120 Â°C <br>@Thickness >=0.750 mm	248 Â°F <br>@Thickness >=0.0295 in
	120 Â°C <br>@Thickness >=1.50 mm	248 Â°F <br>@Thickness >=0.0591 in
	120 Â°C <br>@Thickness >=3.00 mm	248 Â°F <br>@Thickness >=0.118 in
UL RTI, Mechanical without Impact	120 Â°C <br>@Thickness >=0.750 mm	248 Â°F <br>@Thickness >=0.0295 in
	120 Â°C <br>@Thickness >=1.50 mm	248 Â°F <br>@Thickness >=0.0591 in
	120 Â°C <br>@Thickness >=3.00 mm	248 Â°F <br>@Thickness >=0.118 in
Flammability, UL94	V-0 <br>@Thickness >=0.750 mm	V-0 <br>@Thickness >=0.0295 in
	V-0 <br>@Thickness >=1.50 mm	V-0 <br>@Thickness >=0.0591 in
	V-0 <br>@Thickness >=3.00 mm	V-0 <br>@Thickness >=0.118 in

Electrical Properties	Metric	English	Comments
Arc Resistance	60 - 120 sec	60 - 120 sec	ASTM D495
Hot Wire Ignition, HWI	7.0 - 15 sec <br>@Thickness >=0.750 mm	7.0 - 15 sec <br>@Thickness >=0.0295 in
	15 - 30 sec <br>@Thickness >=1.50 mm	15 - 30 sec <br>@Thickness >=0.0591 in
	30 - 60 sec <br>@Thickness >=3.00 mm	30 - 60 sec <br>@Thickness >=0.118 in
High Amp Arc Ignition, HAI	>= 120 arcs <br>@Thickness 0.750 mm	>= 120 arcs <br>@Thickness 0.0295 in
	>= 120 arcs <br>@Thickness 1.50 mm	>= 120 arcs <br>@Thickness 0.0591 in
	>= 120 arcs <br>@Thickness 3.00 mm	>= 120 arcs <br>@Thickness 0.118 in

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	190 - 210 Â°C	374 - 410 Â°F	Injection Molding
Middle Barrel Temperature	200 - 230 Â°C	392 - 446 Â°F	Injection Molding
Front Barrel Temperature	200 - 230 Â°C	392 - 446 Â°F	Injection Molding
Nozzle Temperature	210 - 230 Â°C	410 - 446 Â°F	Injection Molding
Melt Temperature	200 - 230 Â°C	392 - 446 Â°F	Injection Molding
Mold Temperature	40.0 - 60.0 Â°C	104 - 140 Â°F	Injection Molding
Drying Temperature	70.0 - 80.0 Â°C	158 - 176 Â°F	Injection Molding
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour	Injection Molding
Back Pressure	29.4 - 58.8 MPa	4260 - 8530 psi	Injection Molding
Screw Speed	30 - 60 rpm	30 - 60 rpm	Injection Molding