LG Chemical Lupox® PBT-GP-1000 High Flow PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® PBT-GP-1000 High Flow PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | 24 hours at 73°F; ASTM D570 |
| Linear Mold Shrinkage | 0.012 - 0.021 cm/cm | 0.012 - 0.021 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 56.5 MPa @Thickness 3.17 mm |
8190 psi @Thickness 0.125 in |
ASTM D638 |
| Tensile Strength, Yield | 53.8 MPa | 7800 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Yield Strength | 83.4 MPa | 12100 psi | ASTM D570 |
| Flexural Modulus | 2.25 GPa | 327 ksi | ASTM D570 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 0.7937 mm |
HB @Thickness 0.03125 in |
UL94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 225 - 235 °C | 437 - 455 °F | |
| Middle Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Nozzle Temperature | 235 - 249 °C | 455 - 480 °F | |
| Melt Temperature | 235 - 249 °C | 455 - 480 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Surface |
| Drying Temperature | 120 °C | 248 °F | 5 hr. |
| 140 °C | 284 °F | 3 hr. | |
| 120 °C @Time 18000 sec |
248 °F @Time 5.00 hour |
||
| 140 °C @Time 10800 sec |
284 °F @Time 3.00 hour |
||
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Vent Depth | 0.00254 - 0.00381 cm | 0.00100 - 0.00150 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ram Speed Setting | Medium to Fast | |
| Screw Speed | Slow to Medium |
Users viewing this material also viewed the following:
- Poco Graphite ZXF-5Q Industrial Grade Graphite
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 70 lb
- SMAC CABLE® 2519S-40-08 Damping Material
- Techmer ES HiFill® HDPE GF40 40% Glass Filled
- Borealis GD310U Polypropylene Compound, Glass Fiber Reinforced
- ExxonMobil Escorene® UL 8705 Adhesive Application Resin
- DuPont Teijin Films Melinex® 314 Polyester Film, 92 Gauge
- Barlog Plastics KEBAFLEX SG 45 A.1 TPE-S, Shore A45, natural
- Axiall 02541 Plenum Flexible PVC
- 3M Nextel™ AF-11 w/o sizing Aerospace Woven Fabric 312
Copyright © lookpolymers.com All Rights Reserved