LG Chemical Lupox® TE5000H PBT+PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® TE5000H PBT+PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT+PC, High Impact, Dimensional StabilityApplication: Automotive ItemCAS No. 9003-01-04, 24968-12-5 and 103598-77-2Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm @Thickness 3.20 mm |
0.0070 - 0.010 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 59.8 MPa @Thickness 3.20 mm |
8680 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 100 % @Thickness 3.20 mm |
>= 100 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 83.4 MPa @Thickness 6.40 mm |
12100 psi @Thickness 0.252 in |
50mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa @Thickness 6.40 mm |
313 ksi @Thickness 0.252 in |
50mm/min; ASTM D790 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 6.40 mm, Temperature -30.0 °C |
2.76 ft-lb/in @Thickness 0.252 in, Temperature -22.0 °F |
ASTM D256 |
| 5.88 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
11.0 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Front Barrel Temperature | 255 - 265 °C | 491 - 509 °F | Injection Molding |
| Nozzle Temperature | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| Melt Temperature | 260 - 270 °C | 500 - 518 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 120 °C | 248 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3865B TPE, PP Overmold or Standalone use
- Nitriflex Nitrigum 50 FA Styrene Butadiene Rubber
- LATI Laticonther 52/11 GR/70 PP Homopolymer
- Süd-Chemie Nanofil® 5 Flame Retardant
- Techmer ES Electrablend® PA6 CF30 TL10 30% Carbon Filled
- Vyncolit X655 Novolac Phenolic
- BASF 2-(2-Aminoethoxy) ethanol
- Aremco Aremco-Bond™ 2300 High Performance Epoxide
- Asahi Kasei Thermylene® P7-20FG-0876 Chemically Coupled Polypropylene Compound, 20% Glass Filled
- Axiall 390 Coax & Telecom Flexible PVC
Copyright © lookpolymers.com All Rights Reserved