Lanxess Durethan® BCF 30 X H2.0 901510 Nylon 6, 30% Glass + Carbon Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BCF 30 X H2.0 901510 Nylon 6, 30% Glass + Carbon Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 30% reinforced (glass fibers + carbon fibers), conductive, intrinsic color black, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0021 cm/cm | 0.0021 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0059 cm/cm | 0.0059 in/in | ISO 294-4, 2577 |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
| 180 MPa | 26100 psi | ISO 527-1/-2 | |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527-1/-2 |
| 3.5 % | 3.5 % | Nominal; ISO 527-1/-2 | |
| Tensile Modulus | 6.30 GPa | 914 ksi | Conditioned; ISO 527-1/-2 |
| 12.5 GPa | 1810 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Puncture Energy | 2.40 J | 1.77 ft-lb | ISO 6603-2 |
| 1.70 J @Temperature -30.0 °C |
1.25 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 1.70 J @Temperature -30.0 °C |
1.25 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 218 °C | 424 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 140 °C | 284 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Increased electrical conductivity | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA6, MHR, 14-120, (GF+CF)30 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Pacific Sintered Materials F-200-P Iron Powdered Metal
- LNP Emi-X® OC-1008 LEX Polyphenylene Sulfide, Carbon Fiber Reinforcement (discontinued **)
- Lanxess Durethan® BKV 30 H2.0 EF 000000 Nylon 6, Glass Fiber Reinforced
- Lubriplate NO.3V Petroleum-Based Machine Tool Oil
- Solvay Chemicals NOCOLOK® Binder (water-based)
- SABIC Innovative Plastics Xenoy® 6370 PBT+PC (Europe-Africa-Middle East)
- A. Schulman ComAlloy Comtuf® 630 Nylon 6/6, Glass Reinforced, Impact Modified, Flow Enhanced
- BASF Elastollan 890 AN TPUR
- Asahi Kasei Thermofil P-10CC-1417 10% Calcium Carbonate Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved