Plastcom SLOVAMID® 6 T 30 FRC 4 TS PA6 flame retarded, heat stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled , Nylon 6, Heat Stabilized
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID® 6 T 30 FRC 4 TS PA6 flame retarded, heat stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6 for injection molding, reinforced with 30% mineral filler, flame retarded with nonhalogen flame retardant, heat stabilized. Main features: flammability in accordance with UL 94 3 at 1,6 mm, glow wire at 960°C. Application for the electrical industry: protectors, coil forms, covers, terminals. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
STN EN ISO 1183-1
Filler Content 30 %
30 %
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
STN EN ISO 294-4
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa
13800 psi
STN EN ISO 527-2
Elongation at Break 3.0 %
3.0 %
STN EN ISO 527-2
Tensile Modulus 6.70 GPa
972 ksi
STN EN ISO 527-2
Flexural Strength 185 MPa
26800 psi
STN EN ISO 178
Flexural Modulus 5.30 GPa
769 ksi
STN EN ISO 178
Charpy Impact Unnotched 3.00 J/cm²

@Temperature -20.0 °C
14.3 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
3.50 J/cm²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.150 J/cm²

@Temperature -20.0 °C
0.714 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
STN EN ISO 75-2 (A)
Vicat Softening Point 255 °C
491 °F
STN EN ISO 306
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
Glow Wire Test 960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
STN EN 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
STN 34 6460
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
STN 34 6460
Dielectric Strength 40.0 kV/mm
1020 kV/in
STN EN 60243-2
Comparative Tracking Index 600 V
600 V
STN EN 60112
Processing Properties Metric English Comments
Melt Temperature 230 - 250 °C
446 - 482 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 3344
Injection Pressure 50.0 - 90.0 MPa
7250 - 13100 psi