Premix Thermoplastics PRE-ELEC® ESD 7140 Static Dissipative Thermoplastic Compound

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer	Premix Thermoplastics Inc.
Trade Name	PRE-ELEC®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Premix Thermoplastics PRE-ELEC® ESD 7140 Static Dissipative Thermoplastic Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PRE-ELEC® ESD 7140 is a static dissipative thermoplastic masterbatch based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD 7140 has been developed for injection moulding. The products made out of PRE-ELEC® ESD 7140 are washable, reusable and recyclable. Surface resistance values of 108 ohms (IEC 61340-5-1, EOS/ESD S11.11-1993) can be achieved with optimum processing parameters.Applications: Trays, tote bins, crates and technical parts which give permanent ESD protection for the electronics, medical, pharmaceutical and paper handling industries. PRE-ELEC® ESD 7140 can be coloured into various bright colours.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/in³
Thickness	102 microns	4.00 mil
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ISO 294-4
Melt Flow	32 g/10 min @Load 5.00 kg, Temperature 200 °C	32 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength	26.0 MPa	3770 psi	ISO 527
Tensile Strength, Yield	33.0 MPa	4790 psi	ISO 527
Elongation at Break	38 %	38 %	ISO 527
Elongation at Yield	5.0 %	5.0 %	ISO 527
Modulus of Elasticity	1.70 GPa	247 ksi	ISO 178
Izod Impact, Notched (ISO)	9.00 kJ/m² @Thickness 4.00 mm, Temperature -20.0 °C	4.28 ft-lb/in² @Thickness 0.157 in, Temperature -4.00 °F	ISO 180
	24.0 kJ/m² @Thickness 4.00 mm, Temperature 23.0 °C	11.4 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F	ISO 180
Izod Impact, Unnotched (ISO)	NB @Thickness 4.00 mm, Temperature 23.0 °C	NB @Thickness 0.157 in, Temperature 73.4 °F	ISO 180
	NB @Thickness 4.00 mm, Temperature -20.0 °C	NB @Thickness 0.157 in, Temperature -4.00 °F	ISO 180

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	85.0 °C	185 °F	75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi)	73.0 °C	163 °F	75/Method Af

Electrical Properties	Metric	English	Comments
Surface Resistance	<= 1.00e+9 ohm	<= 1.00e+9 ohm	Test specimen: 100mm x 100mm x 3mm molded plaque; ISO IEC 61340-5-1
Static Decay	<= 2.0 sec	<= 2.0 sec	From 1000 V down to 100 V, Test specimen: 100mm x 100mm x 3mm molded plaque; ISO IEC 61340-5-1

Processing Properties	Metric	English	Comments
Processing Temperature	<= 220 °C	<= 428 °F
Melt Temperature	190 - 210 °C	374 - 410 °F
Mold Temperature	30.0 - 70.0 °C	86.0 - 158 °F
Drying Temperature	70.0 - 80.0 °C	158 - 176 °F	Pre-drying in a dehumidifier
Dry Time	3 - 4 hour	3 - 4 hour
Moisture Content	<= 0.15 %	<= 0.15 %	when produced
Injection Pressure	75.2 - 120 MPa	10900 - 17400 psi
Hold Pressure	40.0 - 60.0 MPa	5800 - 8700 psi	Post Pressure
Shelf Life	12.0 Month	12.0 Month	Normal Storing Conditions

Descriptive Properties	Value	Comments
Appearance	Granule
Colour	Whitish
Injection Speed	Moderate

Users viewing this material also viewed the following: