Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Asia Pacific) Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | ISO 178, ASTM D790 |
Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer Description: Nilamid A H2 FR HF2 is an unfilled, flame retardant NYLON 66/6 co-polymer that does not contain halogen or red phosphorous. This product combines excellent flow characteristics and extr.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® CX7010 PC+ABS Cycoloy* CX7010 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0. Excellent flow combined with good balance of pro.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® CX7010 PC+ABS (Asia Pacific) Cycoloy* CX7010 resin is an injection moldable PC/ABS blend. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0. Excellent flow combined with good balance of pro.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® LR900G2 PC (Europe-Africa-Middle East) PC 20% GF Recycle Grade, Preliminary properties |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Lexan® ML7677 PC (Asia Pacific) Transparent Polycarbonate in limited colors. Excellent processability, super high flow, flame retardant, UL rated V-1 at 2.0mm |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® XHT2141 PC Copolymer XHT2141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® XHT2141 PC Copolymer (Europe-Africa-Middle East) XHT2141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Faradex NS0039XP PC+ABS (Europe-Africa-Middle East) LNP* FARADEX* NS0039XP is a compound based on PC/ABS resin containing Stainless Steel Fiber, Flame Retardant. Added features include: Electrically Conductive, EMI/RFI Shielding, Flame retardant.Thi.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
Plaskolite Optix® SG Sign Grade Acrylic Sheet Available in unlimited lengths - no seams in finished products.Data provided by the manufacturer, Plaskolite, Inc. |
|||
Flexural Yield Strength | 110 - 193 MPa | 16000 - 28000 psi | Average value: 142 MPa Grade Count:27 |
Overview of materials for Polycarbonate/ABS Alloy, NCG Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, NCG Fiber Filled". Each property range of values reported is minimum and maximu.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | |
Epoxy Novolac 27%, Carbon fabric 73% Epoxy Novolac - Dow Chemical "DEN 438". Carbon fabric - "VCA" |
|||
Flexural Yield Strength | 110 - 352 MPa | 16000 - 51100 psi | Average value: 253 MPa Grade Count:152 |
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Flexural Yield Strength | 110 - 165 MPa | 16000 - 24000 psi | Average value: 136 MPa Grade Count:3 |
Overview of materials for Nylon 66/6, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are incl.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | ASTM Data |
BASF Capron® 8200CQ Blend Nylon 6 (Dry)
(discontinued **) Capron 8200CQ Blend is a medium viscosity, nylon 6 injection molding homopolymer possessing the combination of strength, stiffness and toughness properties as well as chemical and abrasion resistanc.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM CRS5011R PEI Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM UF5011S PEI Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON Lexan_JK2500 PC+ABS LNP* Stat-kon* Lexan_JK2500 compound is a 20% carbon-fiber reinforced, nonhalogenated red phosporous-free, high-flow FR PC+ABS for EMI/RFI shielding. SE of 21 dB at 1.5 mm. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Noryl LS175 PPE+HIPS (Europe-Africa-Middle East) Noryl* LS175 modified polyphenylene ether resin is an unfilled grade suitable for both extrusion and injection molding conversion routes. It uses non-chlorinated, non-brominated FR additives to del.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL N300X PPE+PS (Asia Pacific) PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL PX1391 PPE+PS (Asia Pacific) Automotive applications, primarily. Excellent electrical properties. high heat. 305F (152C) DTUL. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | ISO 178 |
Wellman Wellamid® 220-N Unfilled Nylon 66, Not Lubricated, Nucleated, or Heat Stabilized Typical Applications: Automotive components, gears, switches, bearings, pulleys, fasteners, electrical coil forms, chain-saw hand guards, cable ties, furniture hardware, small appliance housings, ae.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
Clariant Renol PA213 Nylon 6, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
Clariant Renol PA223G13 Nylon 6, 13% Glass Fiber, Impact Modified Data provided by Clariant Masterbatches |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | 2 mm/min; ISO 178 |
Eurostar Starflam B28UL PA6, Flame Retardant, Injection Molded Starflam B28UL is Unfilled Halogen Free and Red Phosphorous Free, Flame Retardant, Unreinforced Polyamide 6, Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
E-Polymers TEKAMID® TA210 LW TA210LW, Low Wear, Low Friction PA66, DAM Low wear, Low frictionInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Yield Strength | 110 - 262 MPa | 16000 - 38000 psi | Average value: 190 MPa Grade Count:9 |
Overview of materials for Nylon 46, Flame Retarded + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Flame Retarded + Glass Fiber Reinforced". Each property range of values reported is minimum an.. |
|||
Flexural Yield Strength | 110 MPa | 16000 psi | ASTM Data |
BASF Capron® 8202C HS Nylon 6 (Dry)
(discontinued **) Capron 8202C HS is a heat stabilized, low viscosity, polyamide 6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It i.. |
|||
Flexural Yield Strength | 110 - 179 MPa | 16000 - 26000 psi | Average value: 143 MPa Grade Count:4 |
Overview of materials for Acrylic, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values o.. |
|||
Flexural Yield Strength | 110 - 260 MPa | 16000 - 37700 psi | Average value: 177 MPa Grade Count:43 |
Overview of materials for PBT + PET Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "PBT + PET Blend, Glass Filled". Each property range of values reported is minimum and maximum values of .. |