Overview of materials for Nylon 46, Flame Retarded + Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Flame Retarded + Glass Fiber Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 46, Flame Retarded + Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Flame Retarded + Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.47 - 1.87 g/cc
0.0531 - 0.0676 lb/in³
Average value: 1.68 g/cc Grade Count:22
Filler Content 10.0 - 40.0 %
10.0 - 40.0 %
Average value: 25.0 % Grade Count:4
Water Absorption 0.850 - 2.00 %
0.850 - 2.00 %
Average value: 1.14 % Grade Count:9
Moisture Absorption at Equilibrium 1.10 - 2.10 %
1.10 - 2.10 %
Average value: 1.50 % Grade Count:10
Linear Mold Shrinkage 0.00250 - 0.0100 cm/cm
0.00250 - 0.0100 in/in
Average value: 0.00541 cm/cm Grade Count:13
Linear Mold Shrinkage, Transverse 0.00900 - 0.0170 cm/cm
0.00900 - 0.0170 in/in
Average value: 0.0117 cm/cm Grade Count:4
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100 - 120
100 - 120
Average value: 113 Grade Count:6
Tensile Strength, Ultimate 100 - 200 MPa
14500 - 29000 psi
Average value: 150 MPa Grade Count:17
90.0 - 110 MPa

@Temperature 120 - 160 °C
13100 - 16000 psi

@Temperature 248 - 320 °F
Average value: 100 MPa Grade Count:1
Tensile Strength, Yield 82.7 - 131 MPa
12000 - 19000 psi
Average value: 114 MPa Grade Count:5
Elongation at Break 1.00 - 5.50 %
1.00 - 5.50 %
Average value: 2.58 % Grade Count:19
3.00 - 3.00 %

@Temperature 120 - 160 °C
3.00 - 3.00 %

@Temperature 248 - 320 °F
Average value: 3.00 % Grade Count:1
Elongation at Yield 3.00 - 3.80 %
3.00 - 3.80 %
Average value: 3.53 % Grade Count:3
Modulus of Elasticity 5.86 - 18.0 GPa
850 - 2610 ksi
Average value: 11.7 GPa Grade Count:17
6.50 - 9.50 GPa

@Temperature 120 - 160 °C
943 - 1380 ksi

@Temperature 248 - 320 °F
Average value: 8.00 GPa Grade Count:1
Flexural Yield Strength 110 - 262 MPa
16000 - 38000 psi
Average value: 190 MPa Grade Count:9
Flexural Modulus 2.96 - 13.4 GPa
430 - 1950 ksi
Average value: 8.50 GPa Grade Count:13
5.50 - 8.50 GPa

@Temperature 120 - 160 °C
798 - 1230 ksi

@Temperature 248 - 320 °F
Average value: 7.00 GPa Grade Count:1
Izod Impact, Notched 0.427 - 1.33 J/cm
0.800 - 2.50 ft-lb/in
Average value: 0.848 J/cm Grade Count:9
Izod Impact, Unnotched 4.27 - 7.47 J/cm
8.00 - 14.0 ft-lb/in
Average value: 5.87 J/cm Grade Count:4
Izod Impact, Notched (ISO) 12.0 - 12.0 kJ/m²

@Temperature -40.0 - -40.0 °C
5.71 - 5.71 ft-lb/in²

@Temperature -40.0 - -40.0 °F
Average value: 12.0 kJ/m² Grade Count:1
Charpy Impact Unnotched 2.50 - 7.50 J/cm²
11.9 - 35.7 ft-lb/in²
Average value: 5.09 J/cm² Grade Count:9
5.00 - 5.00 J/cm²

@Temperature -30.0 - -30.0 °C
23.8 - 23.8 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 5.00 J/cm² Grade Count:4
Charpy Impact, Notched 0.400 - 1.50 J/cm²
1.90 - 7.14 ft-lb/in²
Average value: 1.07 J/cm² Grade Count:11
0.900 - 1.30 J/cm²

@Temperature -30.0 - -30.0 °C
4.28 - 6.19 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 1.14 J/cm² Grade Count:8
Thermal Properties Metric English Comments
CTE, linear 20.0 - 40.0 µm/m-°C
11.1 - 22.2 µin/in-°F
Average value: 27.7 µm/m-°C Grade Count:14
CTE, linear, Transverse to Flow 45.0 - 80.0 µm/m-°C
25.0 - 44.4 µin/in-°F
Average value: 65.5 µm/m-°C Grade Count:10
Melting Point 295 °C
563 °F
Average value: 295 °C Grade Count:13
Deflection Temperature at 1.8 MPa (264 psi) 123 - 290 °C
254 - 554 °F
Average value: 276 °C Grade Count:18
UL RTI, Electrical 130 - 140 °C
266 - 284 °F
Average value: 138 °C Grade Count:6
Flammability, UL94 V-0
V-0
Grade Count:18
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+8 - 1.00e+15 ohm-cm
1.00e+8 - 1.00e+15 ohm-cm
Average value: 3.02e+14 ohm-cm Grade Count:14
Dielectric Strength 20.0 - 30.0 kV/mm
508 - 762 kV/in
Average value: 25.0 kV/mm Grade Count:14
Comparative Tracking Index 225 - 425 V
225 - 425 V
Average value: 317 V Grade Count:9
Processing Properties Metric English Comments
Processing Temperature 293 - 321 °C
560 - 610 °F
Average value: 307 °C Grade Count:4
Mold Temperature 79.4 - 149 °C
175 - 300 °F
Average value: 114 °C Grade Count:4
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:4