DuPont Performance Polymers Crastin® LW9320 NC010 PBT+SAN  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® LW9320 NC010 PBT+SAN  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9320 NC010 is a 20% glass fiber reinforced polybutylene terephthalate blend for injection molding. It has improved surface aesthetics excellent dimensionalInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
1.34 g/cc
0.0484 lb/in³
ISO 1183
Moisture Absorption 0.300 %

@Thickness 2.00 mm
0.300 %

@Thickness 0.0787 in
Sim. to ISO 62
Viscosity 62350 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
62350 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
ISO 11403-1 -2
70960 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
70960 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
ISO 11403-1 -2
81560 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
81560 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
ISO 11403-1 -2
257200 cP

@Shear Rate 500 1/s,
Temperature 260 °C
257200 cP

@Shear Rate 500 1/s,
Temperature 500 °F
ISO 11403-1 -2
305400 cP

@Shear Rate 500 1/s,
Temperature 250 °C
305400 cP

@Shear Rate 500 1/s,
Temperature 482 °F
ISO 11403-1 -2
362870 cP

@Shear Rate 500 1/s,
Temperature 240 °C
362870 cP

@Shear Rate 500 1/s,
Temperature 464 °F
ISO 11403-1 -2
Viscosity Test 120 cm³/g
120 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
ISO 527-1/-2
Tensile Stress 13.27 MPa

@Strain 1.82 %,
Temperature 150 °C
1925 psi

@Strain 1.82 %,
Temperature 302 °F
ISO 11403-1 -2
16.24 MPa

@Strain 3.01 %,
Temperature 150 °C
2355 psi

@Strain 3.01 %,
Temperature 302 °F
ISO 11403-1 -2
17.67 MPa

@Strain 3.90 %,
Temperature 150 °C
2563 psi

@Strain 3.90 %,
Temperature 302 °F
ISO 11403-1 -2
18.76 MPa

@Strain 4.81 %,
Temperature 150 °C
2721 psi

@Strain 4.81 %,
Temperature 302 °F
ISO 11403-1 -2
19.9 MPa

@Strain 7.50 %,
Temperature 150 °C
2890 psi

@Strain 7.50 %,
Temperature 302 °F
ISO 11403-1 -2
33.89 MPa

@Strain 1.04 %,
Temperature 90.0 °C
4915 psi

@Strain 1.04 %,
Temperature 194 °F
ISO 11403-1 -2
36.62 MPa

@Strain 0.670 %,
Temperature 40.0 °C
5311 psi

@Strain 0.670 %,
Temperature 104 °F
ISO 11403-1 -2
40.46 MPa

@Strain 0.580 %,
Temperature 23.0 °C
5868 psi

@Strain 0.580 %,
Temperature 73.4 °F
ISO 11403-1 -2
44.61 MPa

@Strain 1.73 %,
Temperature 90.0 °C
6470 psi

@Strain 1.73 %,
Temperature 194 °F
ISO 11403-1 -2
49.04 MPa

@Strain 2.25 %,
Temperature 90.0 °C
7113 psi

@Strain 2.25 %,
Temperature 194 °F
ISO 11403-1 -2
51.49 MPa

@Strain 2.76 %,
Temperature 90.0 °C
7468 psi

@Strain 2.76 %,
Temperature 194 °F
ISO 11403-1 -2
56.45 MPa

@Strain 1.12 %,
Temperature 40.0 °C
8187 psi

@Strain 1.12 %,
Temperature 104 °F
ISO 11403-1 -2
57.6 MPa

@Strain 0.824 %,
Temperature 0.000 °C
8350 psi

@Strain 0.824 %,
Temperature 32.0 °F
ISO 11403-1 -2
68.32 MPa

@Strain 1.46 %,
Temperature 40.0 °C
9909 psi

@Strain 1.46 %,
Temperature 104 °F
ISO 11403-1 -2
73.5 MPa

@Strain 1.05 %,
Temperature -20.0 °C
10700 psi

@Strain 1.05 %,
Temperature -4.00 °F
ISO 11403-1 -2
77.56 MPa

@Strain 1.80 %,
Temperature 40.0 °C
11250 psi

@Strain 1.80 %,
Temperature 104 °F
ISO 11403-1 -2
78.81 MPa

@Strain 1.25 %,
Temperature 23.0 °C
11430 psi

@Strain 1.25 %,
Temperature 73.4 °F
ISO 11403-1 -2
87.56 MPa

@Strain 1.35 %,
Temperature 0.000 °C
12700 psi

@Strain 1.35 %,
Temperature 32.0 °F
ISO 11403-1 -2
90.7 MPa

@Strain 2.80 %,
Temperature 40.0 °C
13200 psi

@Strain 2.80 %,
Temperature 104 °F
ISO 11403-1 -2
90.96 MPa

@Strain 1.54 %,
Temperature 23.0 °C
13190 psi

@Strain 1.54 %,
Temperature 73.4 °F
ISO 11403-1 -2
99.91 MPa

@Strain 1.83 %,
Temperature 23.0 °C
14490 psi

@Strain 1.83 %,
Temperature 73.4 °F
ISO 11403-1 -2
105.35 MPa

@Strain 1.73 %,
Temperature 0.000 °C
15280 psi

@Strain 1.73 %,
Temperature 32.0 °F
ISO 11403-1 -2
115.83 MPa

@Strain 2.02 %,
Temperature 0.000 °C
16800 psi

@Strain 2.02 %,
Temperature 32.0 °F
ISO 11403-1 -2
125.72 MPa

@Strain 2.11 %,
Temperature -20.0 °C
18234 psi

@Strain 2.11 %,
Temperature -4.00 °F
ISO 11403-1 -2
135.08 MPa

@Strain 2.40 %,
Temperature -20.0 °C
19592 psi

@Strain 2.40 %,
Temperature -4.00 °F
ISO 11403-1 -2
Elongation at Break 2.5 %
2.5 %
ISO 527-1/-2
Tensile Modulus 7.40 GPa
1070 ksi
ISO 527-1/-2
1.0845 GPa

@Temperature 135 °C
157.29 ksi

@Temperature 275 °F
Dynamic; ISO 11403-1 -2
4.35 GPa

@Temperature 75.0 °C
631 ksi

@Temperature 167 °F
Dynamic; ISO 11403-1 -2
6.17 GPa

@Temperature 45.0 °C
895 ksi

@Temperature 113 °F
Dynamic; ISO 11403-1 -2
7.40 GPa

@Temperature 5.00 °C
1070 ksi

@Temperature 41.0 °F
Dynamic; ISO 11403-1 -2
7.72 GPa

@Temperature -20.0 °C
1120 ksi

@Temperature -4.00 °F
Dynamic; ISO 11403-1 -2
8.21 GPa

@Temperature -45.0 °C
1190 ksi

@Temperature -49.0 °F
Dynamic; ISO 11403-1 -2
8.27 GPa

@Temperature -60.0 °C
1200 ksi

@Temperature -76.0 °F
Dynamic; ISO 11403-1 -2
Flexural Modulus 6.50 GPa
943 ksi
ISO 178
Secant Modulus 3.59 GPa

@Strain 2.47 %,
Temperature 40.0 °C
521 ksi

@Strain 2.47 %,
Temperature 104 °F
ISO 11403-1 -2
4.07 GPa

@Strain 2.02 %,
Temperature 40.0 °C
590 ksi

@Strain 2.02 %,
Temperature 104 °F
ISO 11403-1 -2
4.56 GPa

@Strain 1.57 %,
Temperature 40.0 °C
661 ksi

@Strain 1.57 %,
Temperature 104 °F
ISO 11403-1 -2
5.04 GPa

@Strain 1.12 %,
Temperature 40.0 °C
731 ksi

@Strain 1.12 %,
Temperature 104 °F
ISO 11403-1 -2
5.16 GPa

@Strain 2.02 %,
Temperature 23.0 °C
749 ksi

@Strain 2.02 %,
Temperature 73.4 °F
ISO 11403-1 -2
5.25 GPa

@Strain 2.40 %,
Temperature 0.000 °C
761 ksi

@Strain 2.40 %,
Temperature 32.0 °F
ISO 11403-1 -2
5.456 GPa

@Strain 2.50 %,
Temperature -20.0 °C
791.3 ksi

@Strain 2.50 %,
Temperature -4.00 °F
ISO 11403-1 -2
5.47 GPa

@Strain 0.670 %,
Temperature 40.0 °C
793 ksi

@Strain 0.670 %,
Temperature 104 °F
ISO 11403-1 -2
5.75 GPa

@Strain 1.64 %,
Temperature 23.0 °C
834 ksi

@Strain 1.64 %,
Temperature 73.4 °F
ISO 11403-1 -2
5.96 GPa

@Strain 2.11 %,
Temperature -20.0 °C
864 ksi

@Strain 2.11 %,
Temperature -4.00 °F
ISO 11403-1 -2
5.99 GPa

@Strain 1.82 %,
Temperature 0.000 °C
869 ksi

@Strain 1.82 %,
Temperature 32.0 °F
ISO 11403-1 -2
6.3048 GPa

@Strain 1.25 %,
Temperature 23.0 °C
914.45 ksi

@Strain 1.25 %,
Temperature 73.4 °F
ISO 11403-1 -2
6.49 GPa

@Strain 1.35 %,
Temperature 0.000 °C
941 ksi

@Strain 1.35 %,
Temperature 32.0 °F
ISO 11403-1 -2
6.98 GPa

@Strain 0.580 %,
Temperature 23.0 °C
1010 ksi

@Strain 0.580 %,
Temperature 73.4 °F
ISO 11403-1 -2
6.99 GPa

@Strain 0.824 %,
Temperature 0.000 °C
1010 ksi

@Strain 0.824 %,
Temperature 32.0 °F
ISO 11403-1 -2
7.00 GPa

@Strain 1.05 %,
Temperature -20.0 °C
1020 ksi

@Strain 1.05 %,
Temperature -4.00 °F
ISO 11403-1 -2
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180/1A